Chevrel phase-based solid lubrication coating for wear resistant electrocontact friction pairs in vacuum
نویسندگان
چکیده
The work comparatively studies the wear kinetics of copper friction pairs with Chevrel phase-based coating (Cu-Mo-S) and without it in vacuum 1.5x10−3 Pa. is deposited on test pads by ion-plasma method. tribological investigations scheme were used "disk – coated pad". detected falling rate pair explained change adhesive mechanism to fatigue one.
منابع مشابه
Wear resistant solid lubricant coating made from PTFE and epoxy
A composite coating of polytetrafluoroethylene and epoxy shows 100 · improvements in wear resistance as compared to either of its constituents alone and reduced friction coefficient under testing on a pin-on-disk tribometer. This coating is made by impregnating an expanded PTFE film with epoxy, which provides three unique functions: (1) the epoxy compartmentalizes the PTFE nodes, which is belie...
متن کاملSelf-lubricating, low-friction, wear-resistant Al-based quasicrystalline coatings
After gas atomization, a quasicrystalline powder based on aluminium was used to prepare a thick coating by high-velocity oxygen-fuel flame torch spraying. This layer was deposited on top of a bond-coat layer on a steel plate. A post-spraying annealing treatment turned the two layers to their stable state, a γ-brass crystal and an icosahedral quasicrystal, respectively. The projection parameters...
متن کاملDiamond-like carbon coating under oleic acid lubrication: Evidence for graphene oxide formation in superlow friction
The achievement of the superlubricity regime, with a friction coefficient below 0.01, is the Holy Grail of many tribological applications, with the potential to have a remarkable impact on economic and environmental issues. Based on a combined high-resolution photoemission and soft X-ray absorption study, we report that superlubricity can be realized for engineering applications in bearing stee...
متن کاملFriction Force for Boundary Lubrication
A thermodynamic model describing the phase transition of first order between structure states of lubricant material in the boundary friction regime is proposed. It is shown that lubricant melts with temperature increase or at shear of rubbing surfaces if the elastic strain (stress) exceeds the critical value. The phase diagram with domains of dry and sliding friction is constructed. The depende...
متن کاملFriction and Lubrication
FRICTION AND LUBRICATION in sheet metal forming are influenced by such parameters as material properties, surface finish, temperature, sliding velocity, contact pressure, and lubricant characteristics. The parameters that affect friction and lubrication are schematically shown in Fig. 7.1. Depending on these parameters, the performance of a lubricant and the coefficient of friction (COF) vary. ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Physics: Conference Series
سال: 2021
ISSN: ['1742-6588', '1742-6596']
DOI: https://doi.org/10.1088/1742-6596/1954/1/012039