Charpy impact tenacity of epoxy matrix composites reinforced with aligned jute fibers
نویسندگان
چکیده
منابع مشابه
Impact Properties of Jute and Jute Hybrid Reinforced Composites
The use of natural fiber reinforced composites has continuously increased during recent years due to their low density, low cost and environmental friendliness. At current study, a preliminary investigation on the impact properties and morphologies of unsaturated polyester reinforced by jute woven fabric from the used coffee bags with different moisture contents were carried out. Additionally, ...
متن کاملThermal Degradation of HDPE Short Fibers Reinforced Epoxy Composites
Thermogravimetric analysis was carried out to investigate the thermal degradation of High Density Poly Ethylene (HDPE) short fibers reinforced epoxy composites. Three composites with 5, 10 and 15 % by weight of HDPE short fiber composition were prepared using epoxy as matrix material. The HDPE short fiber used as reinforcing material into the resin helps in retarding the thermal degradation of ...
متن کاملaging influence on charpy impact behavior of basalt fiber reinforced epoxy composites
changes in moisture content and temperature can perturb both stiffness and strength and as such the impact resistance of composite structures. in this paper, the pre-notched basalt fibre reinforced epoxy (bfre) composite specimens are studied under charpy impact loads in order to investigate the changes in impact energy absorption (fracture toughness) with different kinds of aging conditions. t...
متن کاملUltrasonic welding of thermoset matrix composites reinforced with glass fibers using a co-cured retaining layer
In this paper, ultrasonic welding of glass fiber reinforced thermoses, co-cured whit a thermoplastic has been studied. Co-curing process forms a connection between the thermoset and the thermoplastic while curing the composite. Considering that the calculated stress should not be related to the dimensions of the sample, a horn with a tip dimension smaller than the standard overlap was used. The...
متن کاملUltrasonic welding of thermoset matrix composites reinforced with glass fibers using a co-cured retaining layer
In this paper, ultrasonic welding of glass fiber reinforced thermoses, co-cured whit a thermoplastic has been studied. Co-curing process forms a connection between the thermoset and the thermoplastic while curing the composite. Considering that the calculated stress should not be related to the dimensions of the sample, a horn with a tip dimension smaller than the standard overlap was used. The...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Materials Research and Technology
سال: 2017
ISSN: 2238-7854
DOI: 10.1016/j.jmrt.2017.08.004