Characterizations of multilayer ZnO thin films deposited by sol-gel spin coating technique
نویسندگان
چکیده
منابع مشابه
Effects of Cobalt Doping on Optical Properties of ZnO Thin Films Deposited by Sol–Gel Spin Coating Technique
Cobalt (Co) doped Zinc Oxide (ZnO) thin films, containing different amountof Cobalt nanoparticles as the Co doping source, deposited by the sol–gel spin coatingmethod onto glass via annealing temperature at 400˚C, have been investigated by opticalcharacterization method. The effect of Co incorporation on the surface morphology wasclearly observed from scanning electron microscopy (SEM) images. ...
متن کاملTin-doped indium oxide thin films deposited by sol–gel dip-coating technique
Indium tin oxide (ITO) thin films were prepared by the sol–gel dip-coating (SGDC) technique. The microstructure and electrical properties of ITO thin films crystallized using rapid thermal annealing (RTA) were compared with those of films prepared by classic thermal annealing (CTA). ITO thin films were successfully prepared by CTA at 500 jC for 30–60 min. At the same temperature of 500 jC and w...
متن کاملSol-gel spin coating derived ZnO thin film to sense the acetic acid vapor
ZnO thin film of 80 nm thickness was deposited by the sol-gel spin coating method on SiO2/Si substrate and subsequently post-annealed at 500°C with a flow of oxygen for 60 min. Crystallographic structure of the sample was characterized by X-ray diffraction (XRD) method while a field emission scanning electron microscope (FESEM) was used to investigate the surface physical morphology ...
متن کاملSol-gel spin coating derived ZnO thin film to sense the acetic acid vapor
ZnO thin film of 80 nm thickness was deposited by the sol-gel spin coating method on SiO2/Si substrate and subsequently post-annealed at 500°C with a flow of oxygen for 60 min. Crystallographic structure of the sample was characterized by X-ray diffraction (XRD) method while a field emission scanning electron microscope (FESEM) was used to investigate the surface physical morphology ...
متن کاملZnO films prepared by modified sol-gel technique
Zinc oxide films with different thicknesses have been synthesized by modified sol-gel technique. The films are polycrystalline in nature with average grain size between 32 and 57 nm. The thicker films are less strained than the thinner ones. The optical band gap of the films is ~ 3.22 eV. PL spectra are dominated by a strong luminescence peak at ~387 nm followed by a low intensity peak ~469 nm....
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Results in Physics
سال: 2017
ISSN: 2211-3797
DOI: 10.1016/j.rinp.2016.12.029