Characterization of vacuum plasma spray NiCoCrAlY coating resistant to high temperature oxidation
نویسندگان
چکیده
منابع مشابه
High-temperature degradation of plasma sprayed thermal barrier coating systems
Thermal barrier coating systems (TBCs) are used in gas turbines to prevent high-temperature degradation of metallic materials in the combustor and turbine. One of the main concerns regarding TBCs is poor reliability, and accurate life prediction models are necessary in order to fully utilise the beneficial effects of TBCs. This research project aims at developing deeper understanding of the deg...
متن کاملMicrostructure formation in plasma-sprayed functionally graded NiCoCrAlY/yttria-stabilized zirconia coatings
Functionally graded NiCoCrAlY/yttria-stabilized zirconia coatings were fabricated by plasma spraying using mechanically alloyed, plasma-spheroidized NiCoCrAlY/yttria-stabilized zirconia (YSZ) composite powders. Scanning electron microscopy (SEM) and energy dispersive X-ray spectrometry (EDS) analysis revealed that oxidation of aluminum, chromium and yttrium in the NiCoCrAlY alloy occurred in th...
متن کاملTHE OXIDATION RESISTANCE OF HIGH ALUMINUM HEAT RESISTANT STEELS
Abstract: In this research, the oxidation behaviour of high Aluminum heat resistant steel (%25Cr,%20Ni,%8Al) hasbeen evaluated at the temperature range of (1000-1300ºC).The results showed that there was no countinous healinglayer on the surface of the alloy when Al increased up to %5.5 and the oxidation resistance of steel decreased due toformation of spinel oxides on the surface.By increasing ...
متن کاملNickel Base Superalloy Rene®80 – The Effect of High Temperature Cyclic Oxidation on Platinum-Aluminide Coating Features
Nickel base superalloy alloys are used in the manufacture of gas turbine engine components, which in use are exposed to high temperatures and corrosive environments. The platinum aluminide coatings described here have been developed to protect nickel base superalloy alloys from oxidation. In this study, the effect of cyclic oxidation, platinum layer thickness and aluminizing process on beha...
متن کاملCoating Deposition Using Vacuum Arc and Ablation Metal Plasma
An innovative concept in the development of advanced coating deposition and ion implantation method including an application of filtered DC metal plasma or ablation plasma and highfrequency short-pulsed negative bias voltage with a duty factor in the range 10–99% are considered. It was shown that plasma based ion implantation as well as ion-assisted coating deposition may be realized for metal ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Zastita materijala
سال: 2019
ISSN: 0351-9465,2466-2585
DOI: 10.5937/zasmat1904336m