Characterization of pulsed dc magnetron sputtering plasmas
نویسندگان
چکیده
منابع مشابه
CrNx Films Prepared by DC Magnetron Sputtering and High-Power Pulsed Magnetron Sputtering: A Comparative Study
CrNx (0 ≤ x ≤ 0.91) films synthesized using highpower pulsed magnetron sputtering, also known as high-power impulse magnetron sputtering (HiPIMS), have been compared with those made by conventional direct-current (dc) magnetron sputtering (DCMS) operated at the same average power. The HiPIMS deposition rate relative to the DCMS rate was found to decrease linearly with increasing emission streng...
متن کاملPulsed DC Power Supplies for Dual Magnetron Sputtering
Key features of this waveform are the voltage boost period following each polarity transition and fast current rise time due to that boost. Ideally, the boost voltage would be adjustable. It is expected that adjusting the boost voltage will enable some tuning of the film properties, since it will effectively allow tuning of ion energy within the process. Additionally, adjustable duty, the ratio...
متن کاملHigh-rate low-temperature dc pulsed magnetron sputtering of photocatalytic TiO2films: the effect of repetition frequency
The article reports on low-temperature high-rate sputtering of hydrophilic transparent TiO2thin films using dc dual magnetron (DM) sputtering in Ar + O2mixture on unheated glass substrates. The DM was operated in a bipolar asymmetric mode and was equipped with Ti(99.5) targets of 50 mm in diameter. The substrate surface temperature Tsurfmeasured by a thermostrip was less than 180 °C for all exp...
متن کاملPulsed DC bias effects on p-type semiconductor SrCu2O2 film deposited by RF magnetron sputtering.
Transparent p-type semiconducting SrCu2O2 films have been deposited by RF magnetron sputtering under unbalanced bipolar pulsed DC bias on low-alkali glass substrates in a mixed gas of 1% H2/Ar below 400 degrees C. The pulsed DC bias voltages to substrate were varied from 0 V to -200 V with a frequency of 350 kHz. The effect of pulsed DC bias on the structure and electrical and optical propertie...
متن کاملDEPOSITION OF THIN TiO2 FILMS BY DC MAGNETRON SPUTTERING METHOD
Sputter deposition process is another old technique being used in modern semiconductor industries. Sputtering is a process that can deposit TiO2 material on wafer/glass substrates. In this process target is connected to negative high voltage. Further argon gas is introduced into the chamber and is ionized to a positive charge. The positively charged argon atoms are attracted and strike the nega...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: New Journal of Physics
سال: 2005
ISSN: 1367-2630
DOI: 10.1088/1367-2630/7/1/090