Characterization of Porous Magnesium Prepared by Powder Metallurgy - Influence of Powder Shape
نویسندگان
چکیده
منابع مشابه
Porous, Superelastic NiTi Produced by Powder-Metallurgy
Near-stoichiometric NiTi was foamed in the solid state at elevated temperatures through creep expansion of highpressure argon pores previously entrapped during powder consolidation. A sample with 17% porosity was found to be superelastic up to a compressive stress of 800 MPa.
متن کاملFracture Mechanism of CoCrMo Porous Nano-composite Prepared by Powder Metallurgy Route
The main aim of this research was to find the mechanism for the failure of the CoCrMo porous nano-composite by characterizing microstructural changes and fractured surface after compression test. For this purpose, porous nano-composites were prepared with the addition of bioactive glass nano-powder to Co-base alloy with 22.5% porosity by the combination of space-holder and powder metallurgy tec...
متن کاملPorous Titanium Scaffolds Produced by Powder Metallurgy for Biomedical Applications
Department of Bioscience and Buccal Diagnosis, São Jose dos Campos School of Dentistry, State University of São Paulo – UNESP, Av. Engenheiro Francisco José Longo, 777, 12245-000 São José dos Campos SP, Brazil National Institute of Technology, Av. Venezuela, 200, Centro, Rio de Janeiro RJ, Brazil Department of Materials, Air and Space Institute, CTA, Praça Mal. do Ar Eduardo Gomes, 14, 12904-00...
متن کاملPorous NiTi alloy prepared from elemental powder sintering
An elemental powder sintering (EPS) technique has been developed for the synthesis of porous NiTi alloy, in which Ni and Ti powders are used as the reactants and TiH2 powder is added as a pore-forming agent and active agent. Effects of various experimental parameters (sintering temperature, sintering time, and TiH2 content) on the porosity, pore size and pore distribution as well as phase compo...
متن کاملB4C-Al Composites Fabricated by the Powder Metallurgy Process
Due to the large thermal neutron absorption cross section of 10B, B4C-Al composites have been used as neutron absorbing materials in nuclear industries, which can offer not only good neutron shielding performance but also excellent mechanical properties. The distribution of B4C particles affects the mechanical performance and efficiency of the thermal neutron absorption of the composite materia...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Manufacturing Technology
سال: 2014
ISSN: 1213-2489,1213-2489
DOI: 10.21062/ujep/x.2014/a/1213-2489/mt/14/3/271