Characterization Of Oxide Layers Produced On The AISI 321 Stainless Steel After Annealing

Biomaterial Studies on AISI 316L Stainless Steel after Magnetoelectropolishing

The polarisation characteristics of the electropolishing process in a magnetic field (MEP – magnetoelectropolishing), in comparison with those obtained under standard/conventional process (EP) conditions, have been obtained. The occurrence of an EP plateau has been observed in view of the optimization of MEP process. Up-to-date stainless steel surface studies always indicated some amount of fre...

The Electrochemical Behavior of AISI 321 Stainless Steel in Alkaline Media

In this paper, the electrochemical behaviour of passive films formed on AISI 321 stainless steel (AISI 321) immersed in 0.1 M NaOH + 0.1 M KOH solution was evaluated by different electrochemical techniques. For this purpose, passive films were formed at open circuit potential for 1 to 12 hours and then electrochemical measurements were done. The polarization curves suggested that AISI 321 showe...

Microstructural Evolution and Mechanical Properties of Ultrafine/nano Structured AISI 321 Stainless Steel Produced by Thermo-mechanical Processing

The mechanical properties and microstructural developments of 321 stainless steel during thermomechanical process were investigated. The repetitive cold rolling and subsequent annealing were conducted to achieve nanocrystalline structure in an AISI 321 stainless steel. Heavily cold rolling at −20°C was conducted to form martensite in metastable austenitic steel. The process was followed by anne...

The Effect of Solution Concentration on the Electrochemical Behaviour of AISI 321 Stainless Steel in Sulfuric Solutions

EFFECT OF IMMERSION TIME ON THE ELECTROCHEMICAL BEHAVIOUR OF AISI 321 STAINLESS STEEL IN 0.1 M H2SO4 SOLUTION

In this study, effect of immersion time on the electrochemical behaviour of AISI 321 stainless steel (AISI 321) in 0.1 M H 2SO 4 solution under open circuit potential (OCP) conditions was evaluated by potentiodynamic polarization, Mott–Schottky analysis and electrochemical impedance spectroscopy (EIS). Mott–Schottky analysis revealed that the passive films behave as n-type and p-type s...