Characterization of Nano-Silica Local Metakaolin Based-Geopolymer: Microstructure and Mechanical Properties
نویسندگان
چکیده
منابع مشابه
Performance Evaluation and Microstructure Characterization of Metakaolin-Based Geopolymer Containing Oil Palm Ash
This study reports on the microstructure, compressive strength, and drying shrinkage of metakaolin (MK) based geopolymers produced by partially replacing MK by oil palm ash (OPA). The OPA was used as raw material producing different molar ratios of SiO₂/Al₂O₃ and CaO/SiO₂. The geopolymer samples were cured at 80°C for 1, 2, or 4 hours and kept at ambient temperature until testing. The compressi...
متن کاملPreparation and Properties of Alkali Activated Metakaolin-Based Geopolymer
The effective activation and utilization of metakaolin as an alkali activated geopolymer precursor and its use in concrete surface protection is of great interest. In this paper, the formula of alkali activated metakaolin-based geopolymers was studied using an orthogonal experimental design. It was found that the optimal geopolymer was prepared with metakaolin, sodium hydroxide, sodium silicate...
متن کاملEffects of Nano-SiO2 on Setting Time and Compressive Strength of Alkali- activated Metakaolin-based Geopolymer
This study presents a discussion on the effects of different solid-to-liquid (S/L) ratios (0.97 to 1.19) and nanoSiO2 (NS) percentages (0% to 3%) on some properties of metakaolin (MK)-based geopolymers. The setting time and compressive strength were investigated. Mercury intrusion porosimetry, fourier transform infrared spectroscopy, and scanning electron microscopy were used to determine the m...
متن کاملMechanical Properties and Microstructure of Class C Fly Ash-Based Geopolymer Paste and Mortar
This paper presents workability, compressive strength and microstructure for geopolymer pastes and mortars made of class C fly ash at mass ratios of water-to-fly ash from 0.30 to 0.35. Fluidity was in the range of 145-173 mm for pastes and 131-136 mm for mortars. The highest strengths of paste and mortar were 58 MPa and 85 MPa when they were cured at 70 °C for 24 h. In XRD patterns, unreacted q...
متن کاملMicrostructure Characterization and Mechanical Properties of Al-SiCp Composites
In recent years the aluminum matrix composites are gaining wide spread applications in automotive, aerospace, defense, sport and other industries. The reason for this is their exciting properties like high specific strength, stiffness, hardness, wear resistance, dimensional stability and designer flexibility. The present work reports on mechanical properties and microstructure analysis of Al-Si...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Open Journal of Civil Engineering
سال: 2020
ISSN: 2164-3164,2164-3172
DOI: 10.4236/ojce.2020.102013