Characterization and kinetic modeling of secondary phases in squeeze cast Al alloy A380 by DSC thermal analysis
نویسندگان
چکیده
منابع مشابه
Morphological and Thermal Flux Analysis in as-Cast Al Alloy after Swarf Addition
In this research, effect of swarf addition on the microstructure of die cast aluminum A380 alloy and the possibility of altering the alloy structure in the metallic die has been studied. The microstructure mainly consists of the α-phase, eutectic, intermetallic compounds and porosity. Since the alloy solidifies under non-equilibrium conditions, the Scheil equation with exact amount of equilibri...
متن کاملEnhancing Wear Resistance of Squeeze Cast AC2A Aluminum Alloy
The effect of squeeze casting process parameters on wear behavior of AC2A aluminium alloy was primarily investigated in this experimental study. Five process parameters, namely squeeze pressure, pouring temperature, die temperature, die material and compression time, each at four levels were chosen and sixteen experimental runs based on L16 orthogonal array were performed. From analysis of vari...
متن کاملsuppression of coke formation in thermal cracking by coke inhibitors
the main purpose of this research was to:1.develop a coking model for thermal cracking of naphtha.2.study coke inhibition methods using different coke inhibitors.developing a coking model in naphtha cracking reactors requires a suitable model of the thermal cracking reactor based on a reliable kinetic model.to obtain reliable results all these models shall be solved simultaneously.for this pu...
15 صفحه اولFailure Analysis of a Cast A380 Aluminum Alloy Casting Using a Microstructurally Based Fatigue Model
When evaluating the fatigue life of a die cast A380 aluminum alloy, the combination of microstructures, inclusions, and stress concentrations is particularly important. This paper presents a failure analysis of an A380 die cast aluminum pivot arm used in a clothing press. This study includes finite element analyses, optical microscopy of the fracture surface, fatigue testing of the A380 aluminu...
متن کاملTHERMAL FATIGUE RESISTANCES OF 356 AND 413 CAST Al ALLOYS
Abstract: Thermal fatigue is a stochastic process often showing considerable scatter even in controlled environments. Due to complexity of thermal fatigue, there is no a complete analytical solution for predicting the effect of this property on the life of various components, subjected to severe thermal fluctuations. Among these components, one can mention car cylinder, cylinder head and pi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: China Foundry
سال: 2017
ISSN: 1672-6421,2365-9459
DOI: 10.1007/s41230-017-6092-4