Characterization and antibacterial activity of nickel ferrite doped α-alumina nanoparticle
نویسندگان
چکیده
منابع مشابه
Transmission Electron Microscopy (TEM) Characterization of doped α-Alumina
Qualitative EDX analysis: A map is acquired in low magnification. Results show equiaxial grains finely distributed through out the sample. In spite of the fact that simulations indicate no clear energetic gain or loss for cosegreation over single dopant segregation in this material, we observed that in all grain boundaries these two dopants (Y an La) are segregating together (figure 2). This co...
متن کاملSynthesis and Characterization of Nickel Zinc Ferrite Nanoparticles
In this research nickel zinc ferrite nanoparticles with composition of Ni1-xZnxFe2O4 (where x=0, 0.3, 0.7, 1) were synthesized by a sol-gel method at 600 °C for 5 hours. The structure of nanoparticles was studied using X-ray diffraction pattern. The lattice parameter of ferrite nanoparticles was calculated and indicates lattice constant of nanoparticl...
متن کاملSynthesis and characterization of Ag doped Cobalt Ferrite nanocomposite
Nanomaterials are attracted a great deal of attention from scientific community due to its unique properties and applications. The small size ferrites have opened the door for intensive research to utilize their properties for biomedical applications. Cobalt ferrite nanomaterials and its silver doped (Ag-doped) nanocomposites have been prepared using solid state combustion method. This combusti...
متن کاملSynthesis and characterization of Nickel Copper Ferrite
Nano size nickel copper ferrite powders (NiCuFe2O4) have been prepared by a prepared by Co precipitation method. The resulting powders were characterized by X-ray diffraction (XRD), Scanning electron microscope (SEM).The result showed nanosize nickel copper ferrite(35.65nm). The powders showed extensive XRD line broadening and sizes of crystals observed from the XRD line broadening was35.65 nm,...
متن کاملSynthesis and characterization of Lanthanum doped Bismuth Ferrite
B1-xLaxFeO3 (x = 0.0, 0.025) crystallites were prepared by chemical solution route. XRD analysis confirmed the phase formation of the materials. Thermal characterization was done by DSC-TGA to confirm crystallization and thermal behavior for phase development. Morphological studies by FESEM showed the agglomerated nature of the ferrite...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Engineering Science and Technology, an International Journal
سال: 2017
ISSN: 2215-0986
DOI: 10.1016/j.jestch.2016.12.008