Characteristics of Thermal Cycle Damage of FGM Thermal Barrier Coatings in Vacuum.
نویسندگان
چکیده
منابع مشابه
suppression of coke formation in thermal cracking by coke inhibitors
the main purpose of this research was to:1.develop a coking model for thermal cracking of naphtha.2.study coke inhibition methods using different coke inhibitors.developing a coking model in naphtha cracking reactors requires a suitable model of the thermal cracking reactor based on a reliable kinetic model.to obtain reliable results all these models shall be solved simultaneously.for this pu...
15 صفحه اولErosion and Foreign Object Damage of Thermal Barrier Coatings
Thermal barrier coating are perceived as an enabling technology to increase the performance of, improve efficiency within, and lower the emissions from, modern gas turbines. To fully utilise this capability one has to be able to accurately predict the life of these coatings under conditions relevant to gas turbine service. This paper addresses the failure of TBC systems as a result of erosion a...
متن کاملMicrostructural investigations of EBPVD thermal barrier coatings
This paper deals with the morphology, constitutive phases and fine microstructures of some EBPVD processed yttria partially stabilized zirconia thermal barrier coatings. This study has been performed by X-ray diffraction and scanning and transmission electron microscopy. It was shown that the coatings studied were constituted of a single metastable tetragonal t' phase, as expected if one refers...
متن کاملThermophysical properties of thermal barrier coatings
Thin layers of thermal barrier coating (TBCs) are applied to metallic components of heat engines to reduce metal temperatures and to provide environmental protection. This results in increased engine efficiency and prolonged operational life. Of special current interest is the use of TBCs in aircraft engines. The TBCs, often yttria-stabilized zirconia (YSZ), are deposited on nickel or cobalt-ba...
متن کاملDelamination of multilayer thermal barrier coatings
Multilayer thermal barrier coatings (TBCs) on superalloy substrates are comprised of an intermetallic bond coat, a thermally grown oxide (TGO) layer, and a porous zirconia top coat that provides thermal protection. The TGO attains a thickness of 1±10 lm prior to failure, while the bond coat and zirconia layer are each about 50±100 lm thick. The preferred method for manufacturing TBCs comprises ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Society of Materials Science, Japan
سال: 1997
ISSN: 1880-7488,0514-5163
DOI: 10.2472/jsms.46.939