Characteristics of Carbon Material Formation on SBA-15 and Ni-SBA-15 Templates by Acetylene Decomposition and Their Bioactivity Effects
نویسندگان
چکیده
منابع مشابه
Characteristics of Carbon Material Formation on SBA-15 and Ni-SBA-15 Templates by Acetylene Decomposition and Their Bioactivity Effects
Carbon spheres and tubes were formed from acetylene decomposition on SBA-15 and Ni-SBA-15 at 650-850 °C. At 650 °C, the decomposed carbons covered the surface of the support, and no carbon spheres and filament materials were formed. Carbon sphere formation occurred at 750 °C-850 °C; with diameters ranging from 0.8 μm-1.1 μm. For Ni-SBA-15, the diameters of the spheres and filaments were 0.8 μm ...
متن کاملFormation of cyanide-functionalized SBA-15 and its transformation to carboxylate-functionalized SBA-15
Cyanide-functionalized mesoporous silica SBA-15 (CN/SBA-15) with pore diameters larger than 6 nm has been prepared by a one-pot synthesis. The structure of CN/SBA-15 is affected by the amount of the functional silane 2-cyanoethyltriethoxysilane (CTES) and the conditions of co-condensation in the acidic aqueous solution of the triblock copolymer Pluronic P123: whereas direct mixing of the silica...
متن کاملDegradation of trinitroglycerin (TNG) using zero-valent iron nanoparticles/nanosilica SBA-15 composite (ZVINs/SBA-15).
Trinitroglycerin (TNG) is an industrial chemical mostly known for its clinical use in treating angina and manufacturing dynamite. The wide manufacture and application of TNG has led to contamination of vast areas of soil and water. The present study describes degradation of TNG with zero-valent iron nanoparticles (ZVINs) in water either present alone or stabilized on nanostructured silica SBA-1...
متن کاملFormation of titanium nitride nanoparticles within mesoporous silica SBA-15.
We report the first synthesis of titanium nitride (TiN) nanoparticles inside the nanoscale channels of mesoporous silica SBA-15. The TiN precursor, Ti(NMe(2))(4) in toluene, was incorporated into the methyl group-modified channels of the SBA-15 powder. The functionalization of pore surfaces with methyl groups generates hydrophobic surfaces that facilitate impregnation with Ti(NMe(2))(4) and min...
متن کاملTransient Colloidal Stability Controls the Particle Formation of SBA-15
A hypothesis about (transient) colloidal stability as a controlling mechanism for particle formation in SBA-15 is presented. The hypothesis is based on results from both in situ and ex situ investigations, including cryogenic transmission electron microscopy (cryo-TEM), UV-vis spectroscopy, and dynamic light scattering (DLS). Cryo-TEM images show that particles grow via the formation of silica-...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials
سال: 2016
ISSN: 1996-1944
DOI: 10.3390/ma9050350