Changes in spectral characteristics of thin molybdenum films with atmospheric annealing
نویسندگان
چکیده
منابع مشابه
Structural, Electrical and Optical Properties of Molybdenum Oxide Thin Films Prepared by Post-annealing of Mo Thin Films
Molybdenum thin films with 50 and 150 nm thicknesses were deposited on silicon substrates, using DC magnetron sputtering system, then post-annealed at different temperatures (200, 325, 450, 575 and 700°C) with flow oxygen at 200 sccm (standard Cubic centimeter per minute). The crystallographic structure of the films was obtained by means of x-ray diffraction (XRD) analysis. An atomic force micr...
متن کاملStructural, Electrical and Optical Properties of Molybdenum Oxide Thin Films Prepared by Post-annealing of Mo Thin Films
Molybdenum thin films with 50 and 150 nm thicknesses were deposited on silicon substrates, using DC magnetron sputtering system, then post-annealed at different temperatures (200, 325, 450, 575 and 700°C) with flow oxygen at 200 sccm (standard Cubic centimeter per minute). The crystallographic structure of the films was obtained by means of x-ray diffraction (XRD) analysis. An atomic force micr...
متن کاملstructural, electrical and optical properties of molybdenum oxide thin films prepared by post-annealing of mo thin films
molybdenum thin films with 50 and 150 nm thicknesses were deposited on silicon substrates, using dc magnetron sputtering system, then post-annealed at different temperatures (200, 325, 450, 575 and 700°c) with flow oxygen at 200 sccm (standard cubic centimeter per minute). the crystallographic structure of the films was obtained by means of x-ray diffraction (xrd) analysis. an atomic force micr...
متن کاملEffect of Annealing on Physical Properties of Cu2ZnSnS4 (CZTS) Thin Films for Solar Cell Applications
Cu2ZnSnS4 (CZTS) thin films were prepared by directly sputteringCu (In,Ga)Se2 quaternary target consisting of (Cu: 25%, Zn: 12.5%, Sn; 12.5%and S: 50%). The composition and structure of CZTS layers have beeninvestigated after annealing at 200 0C, 350 0C and 500 0C under vacuum. Theresults show that recrystallization of the CZTS thin film occurs and increasingthe grain size with a preferred orie...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Physics: Conference Series
سال: 2016
ISSN: 1742-6588,1742-6596
DOI: 10.1088/1742-6596/735/1/012058