Change of solution chemistry within crevice in crevivce corrosion of stainless steel.
نویسندگان
چکیده
منابع مشابه
Corrosion Behavior of Stainless Steel Clad Rebar
Stainless steel clad rebar (SCR) was investigated because it may become a cost-effective means of controlling corrosion in concrete under very aggressive environments. Sound SCR (316L cladding) resisted corrosion in saturated Ca(OH)2 solution (SCS) with up to 5 wt% chloride. Cladding breaks on SCR induced significant corrosion of exposed underlying CS in SCS with only 1 wt% chloride. A computer...
متن کاملCorrosion at Sulphide Inclusions in Stainless Steel
Auger analysis was performed using a high resolution scanning auger electron microscope and auger electron spectroscopy. Elemental auger contour maps for corroded sulphide inclusions in stainless steel were presented. It was found that the copper enriched-manganese sulphide inclusions were uniformly corroded, which might be due to CU2S deposition on the surface of corroding inclusions. In contr...
متن کاملCorrosion Fatigue of 17-4pH Stainless Steel in a Simulated Sea Water Solution
Since martensitic precipitation hardened 17-4pH stainless steel has been widely used in corrosive environments, evaluation of its corrosion fatigue behavior is important. In this research, after microstructural studies, mechanical, corrosion, fatigue and corrosion fatigue tests were performed on 17-4pH specimens. Fatigue and corrosion fatigue tests were carried out at the stress ratio of -1 an...
متن کاملAn Investigation on Corrosion and Stress Corrosion Cracking initiation of a Ferritic Stainless Steel in a Tertiary Amine Solution
The present study focused on stress corrosion cracking (SCC) and corrosion behavior of ferritic stainless steel (grade 430) in activated methyl diethanolamine (aMDEA) solution, which is classified as a tertiary amine. In this regard, cyclic polarization and U-bend tests were performed in CO2 loaded aMDEA with different concentrations at 25 and 70 °C to observe corrosion behavior and ...
متن کاملCORROSION RESISTANCE OF TiN COATED 316L STAINLESS STEEL IN ARTIFICIAL PHYSIOLOGICAL SOLUTION
The corrosion behavior of TiN coated 316L stainless steel in an artificial physiological solution was investigated by means of an electrochemical test. Two different PVD methods were used for film deposition: cathodic arc and reactive magnetron sputtering. The dependence of the corrosion resistance on the main deposition parameters (nitrogen pressure, substrate bias) was analyzed. For a better ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Society of Materials Science, Japan
سال: 1985
ISSN: 1880-7488,0514-5163
DOI: 10.2472/jsms.34.106