Ceramic Mold-HIP Processing of Nb-Al Intermetallic Powder
نویسندگان
چکیده
منابع مشابه
Production of Dispersed Ceramic Nano-Particles in Al Alloy Using Friction Stir Processing
In this research, surface composite layers containing nano sized TiB2, Al2O3-TiB2, ZrO2 and CNT particles have been fabricated on Aluminum alloy substrates by friction stir processing. The effects of different processing variables such as number of passes and strengthening particle distribution, hardness, and wear properties of surface nano...
متن کاملProduction of Dispersed Ceramic Nano-Particles in Al Alloy Using Friction Stir Processing
In this research, surface composite layers containing nano sized TiB2, Al2O3-TiB2, ZrO2 and CNT particles have been fabricated on Aluminum alloy substrates by friction stir processing. The effects of different processing variables such as number of passes and strengthening particle distribution, hardness, and wear properties of surface nano...
متن کاملElectric Field Gradient at Nb Site in the Intermetallic Compounds
The electric field gradient (efg) at the Nb site in the intermetallic compounds Nb3X (X = Al, In, Si, Ge, Sn) was measured by the Perturbed Angular Correlation (PAC) method using the wellknown gamma-gamma cascade of 133 482 keV inTa from the decay of Hf, substituting approximately 0.1 atom percent of Nb. The PAC results show that Vzz drops by nearly 40% when X changes from Al to In, and by abou...
متن کاملMicrocompression study of Al-Nb nanoscale multilayers
Microcompression tests were performed on the Al/Nb multilayers of incoherent interfaces with the layer thicknesses of 5 nm Al/5 nm Nb and 50 nm Al/50 nm Nb. The Al-Nb multilayers showed increase in strength as the layer thickness was reduced; the average flow stresses at 5% plastic strain from the 5 nm Al/5 nm Nb and 50 nm Al/50 nm Nb layer thickness specimens were determined to be 2.1 GPa and ...
متن کاملRheology of Ceramic-powder-filled Polymer Melts
Ceramic powder (zirconia) was mixed with binder consisting polypropylene, paraffin and stearic acid in elastic extruder. Steady and oscillatory shear flow properties of these materials in the molten state were measured on a cone-plate rheometer; parallel superposed steady and oscillatory shear flow experiments were also carried out. Moreover, flow properties at high shear rates were measured on...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials Transactions, JIM
سال: 1996
ISSN: 0916-1821,2432-471X
DOI: 10.2320/matertrans1989.37.828