CAST IRONS TO-DAY

ASM Specialty Handbook Cast Irons

Fatigue Behaviour of Synthetic Nodular Cast Irons

A. Vaško, L. Trško, R. Konečná, Faculty of Mechanical Engineering, University of Žilina, Žilina, Slovak Republic The paper shows the influence of charge composition on microstructure, fatigue properties and failure micromechanisms of nodular cast irons. The additive of metallurgical silicon carbide (SiC) in analysed specimens increases the content of ferrite in the matrix, decreases the size of...

Microstructural characterization and kinetics modelization of vermicular cast irons

Several experimental techniques are used for phase identification and microstructure characterization of austempered vermicular cast irons (XRD, SEM, TEM and Mössbauer spectroscopy). Acicular structures were found to be composed by ferrite and austenite with average sizes compatible with those reported for bainitic ferrite in steels. An assessment of the free energy change involved in the auste...

Delamination Wear Mechanism in Gray Cast Irons

An investigation of the friction and sliding wear of gray cast iron against chromium plated cast irons was carried out on a newly constructed reciprocating friction and wear tester. The tests were the first to be done on the test rig under dry conditions and at the speed of 170 cm/min, and variable loads of 20-260 N for a duration of 15 min. to 3 hours. The gray cast iron surfaces worn by a pro...

Graphite Morphology’s Influence on Shot Peening Results in Cast Irons

The different shot peening responds of a grey cast iron (GI) with its flake graphite and a compacted cast iron (CGI) with its vermicular graphite was analyzed and compared in this paper. For peening using identical parameters, CGI showed a larger plastic deformation zone with higher subsurface compressive stresses than GI. Electron backscatter diffraction (EBSD) mapping and backscatter electron...