Cassava waste pulp – poly(acrylamide-acrylic acid) based hydrogels using gamma irradiation
نویسندگان
چکیده
منابع مشابه
Acrylic acid and methacrylic acid based hydrogels-A review
Hydrogels are three-dimensional polymeric networks those swell quickly by imbibing a large amount of water or deswell in response to even miniscule changes in their external environment. The water uptake or swelling may be thousands of times of their initial volume in water. The volume phase transitions as a response to different stimuli make these materials interesting objects of scientific ob...
متن کاملSynthesis of pH Sensitive Hydrogels Based on Poly Vinyl Alcohol and Poly Acrylic Acid
In this research, hydrogels based on poly vinyl alcohol and poly acrylic acid blend were prepared which were cross-linked by applied thermal conditions. Afterward, effects of time and heating on water uptake were investigated. The highest water uptake value exhibited by the sample that was heated for 20 min. at 110 ºC was about 2129% after 4 days at equilibrium state. Hydrogels exhibited p...
متن کاملBrillouin light-scattering from poly(acrylic acid) hydrogels
The Brillouin shift and width for poly(acrylic acid) hydrogels have been obtained as a function of gel network volume fraction using a five-pass Fabry-Pdrot interferometer. A conspicuous peak has been observed in the Brillouin shift at high volume fraction. The results are discussed in the light of a theory for the Brillouin light-scattering from gels proposed by Marqusee and Deutch-
متن کاملSynthesis of carboxymethylcellulose/starch superabsorbent hydrogels by gamma-irradiation
BACKGROUND Superabsorbent hydrogels show a large potential in a wide array of applications due to their unique properties. Carboxymethylcellulose (CMC) is a commercially available water-soluble cellulose derivative of major interest in the hydrogel synthesis. High-energy irradiation allows the chemical crosslinking without the use of crosslinking agents, while the introduction of other natural ...
متن کاملsynthesis of ph sensitive hydrogels based on poly vinyl alcohol and poly acrylic acid
in this research, hydrogels based on poly vinyl alcohol and poly acrylic acid blend were prepared which were cross-linked by applied thermal conditions. afterward, effects of time and heating on water uptake were investigated. the highest water uptake value exhibited by the sample that was heated for 20 min. at 110 ºc was about 2129% after 4 days at equilibrium state. hydrogels exhibited ph-sen...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Physics: Conference Series
سال: 2021
ISSN: 1742-6588,1742-6596
DOI: 10.1088/1742-6596/1912/1/012017