Carbide formation in tungsten coatings on carbon-fibre reinforced carbon substrates
نویسندگان
چکیده
منابع مشابه
Carbide formation in tungsten-containing amorphous carbon films by annealing
Tungsten-containing amorphous carbon films were produced by dual magnetron sputter deposition. The formation of carbide phases after heat treatment in inert gas at temperatures up to 2800 K was investigated by X-ray diffraction for tungsten concentrations below 25 at%. After deposition, each film consists of an amorphous carbon matrix with atomically dispersed W inclusions. Annealing up to 2800...
متن کاملCarbon-fibre reinforced plates for problem fractures.
We report our experience with carbon-fibre reinforced plastic (CFRP) plates in the management of 19 problem fractures complicated by either infection, nonunion, comminution or contamination. The combination offers secure fixation without inhibition of callus formation.
متن کاملImage Characterization of Carbon Fibre Reinforced Composites
A new methodology to detect fibres orientation in composite materials, using image processing tools is introduced. Several examples with manufacturing defects are studied using RIMAPS technique and the Variogram method. The characterization is made from digitized images of the samples. Combined use of RIMAPS and Variogram analyses identified the orientation of fibres and determined the values o...
متن کاملWear of ceramic-on-carbon fibre reinforced PEEK hip replacements
Total hip replacement has been a successful surgical intervention for many years. However, concerns regarding UHMWPE wear particle induced osteolysis [1], have led to alternative bearing materials to be sought. Carbon-fibre reinforced poly-ether-ether-ketone (CFR-PEEK) is a fibre-reinforced polymer which has shown reduced wear in hip and knee configurations compared with conventional polyethyle...
متن کاملCarbon-hydrogen bond activation over tungsten carbide catalysts
Tungsten carbides with surface areas ranging from 4 to 39 m2/g were prepared by the temperatureprogrammed carburization of tungsten oxide and nitride powders with pure C H 4 o r a 48.9% CH4 in H 2 mixture. Oxygen uptakes on the carbides were low most likely because of the presence of graphitic carbon at the surface. Nevertheless, the carbides were active and selective for the dehydrogenation of...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Thin Solid Films
سال: 2013
ISSN: 0040-6090
DOI: 10.1016/j.tsf.2012.10.066