STUDY ON VANADIUM CARBIDE COATING FORMATION ON AISI L2 STEEL BY THERMO-REACTIVE DEPOSITION TECHNIQUE
Abstract: The possibility of vanadium carbide coating formation on AISI L2 steel was studied in molten salt bath containing 33 wt% NaCl- 67 wt% CaCl2. In this research, the effects of time, temperature and bath composition on growing layer thickness were studied. The vanadium carbide coating treatment was performed in the NaCl-CaCl2 bath at 1173, 1273 and 1373 K temperatures for 3, 6, 9 hours a...
متن کاملSynthesis and characterization of nHA-PLA composite coating on stainless steel by dip-coating process for biomedical applications
316L stainless steel is the most commonly used metallic material in the manufacture of orthopedic implants. To achive better properties metal implants often coated with biocomposites. A sol–gel method was used for coating of Poly lactic acid (PLA)/Hydroxyapatite nanopowder (nHA) on stainless steel 316L substrate. The X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) wer...
متن کاملSTUDY ON NIOBIUM CARBIDE COATING FORMATION ON AISI L2 STEEL USING THERMO-REACTIVE DEPOSITION METHOD
In the present research, to form niobium carbide coating on the surface of AISI L2 steel Thermo-Reactive Deposition method (TRD) in a molten bath was used. Niobium carbide coating treatment was carried out at 1173 K, 1273 K, and 1373 K for 2, 4, and 8 hours. The molten bath contained 20wt.% borax (Na2B4O7), 5 wt.% boric acid (B2O3), and 75 wt.% ferro-niobium. The presence and properties of...
متن کاملKinetic Study of Niobium Carbide Coating Formation on AISI L2 Steel using Thermo-Reactive Deposition Technique
In the present study, Thermo-Reactive Deposition method (TRD) in a molten bath was used to form niobium carbide coating on AISI L2 steel. The coating was formed in five different composition of borax (Na2B4O7), boric acid (B2O3), and ferro-niobium. For all of the five compositions of molten bath, niobium carbide coating treatment was carried out at 1173 K, 1273 K, and 1373 K for 2, 4 and 8 hour...
متن کاملSurface and Bulk Carbide Transformations in High-Speed Steel
We have studied the transformation of carbides in AISI M42 high-speed steels in the temperature window used for forging. The annealing was found to result in the partial transformation of the large, metastable M2C carbides into small, more stable grains of M6C, with an associated change in the crystal orientation. In addition, MC carbides form during the transformation of M2C to M6C. From the h...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Microscopy and Microanalysis
سال: 2003
ISSN: 1431-9276,1435-8115
DOI: 10.1017/s1431927603443444