Can High-Entropy Interlayers Develop Intermetallic-Free Welded Joints of Dissimilar Metals?
نویسندگان
چکیده
منابع مشابه
Control of Formation of Intermetallic Compound in Dissimilar Joints Aluminum-steel
The elimination of the FexAly type phases was considered the solution to low ductility presented in aluminum-steel welded joints. Recently, the researches do not seek the suppression but the control of the thickness of these compounds. In this work, Al-Fe joints were manufactured by solid state and fusion welding, looking for controlling the formation of intermetallic comp...
متن کاملCharacterization of Diffusion Welded Joints between Titanium and Permendur Type Alloy Using Different Interlayers
The experiments regarding the solid–state diffusion bonded joints prepared between commercialy pure titanium and permendur type soft magnetic alloy are presented. The diffusion bonding of these materials were carried out using copper and nickel interlayers, in the temperature range of 850-950 C for 1,5 hrs., under uniaxial pressure, in argon atmosphere. The microstructure of the transition join...
متن کاملEvaluation Of Mechanical Properties Of Dissimilar Metal Tube Welded Joints Using Inert Gas Welding
Evaluation of welding process such as metal inert gas welding and tungsten inert gas arc welding on tensile, bend and hardness properties of austenitic stainless steel SS347H(18Cr 10Ni 1Cb ), T22(21⁄4Cr Mo) and T91(9Cr 1Mo V) grades are studied. Tubes of 54 mm of outer diameter and 4 mm of wall thickness is used as a base material in the following combination SS347H VS T91 and T91 VS T22 is wel...
متن کاملThe effect of Zn element addition on dissimilar Al6061/AZ31 friction stir welded joints
In this study, friction stir butt welding of Mg and Al alloys with applying Zn interlayer was performed. To obtain optimum condition, a combination of two travel and three rotation speeds were selected. Mg-Zn and Mg-Al-Zn IMCs, Al solid solution and residual Zn, were the most common phases in the stirred zone, which eliminated the formation of Al-Mg intermetallics. The maximum mechanical proper...
متن کاملThe effect of Zn element addition on dissimilar Al6061/AZ31 friction stir welded joints
In this study, friction stir butt welding of Mg and Al alloys with applying Zn interlayer was performed. To obtain optimum condition, a combination of two travel and three rotation speeds were selected. Mg-Zn and Mg-Al-Zn IMCs, Al solid solution and residual Zn, were the most common phases in the stirred zone, which eliminated the formation of Al-Mg intermetallics. The maximum mechanical proper...