Brittle fracture prediction of key-hole notched specimens by means of J-integral expression
نویسندگان
چکیده
منابع مشابه
Influence of Notch Depth-to-Width Ratios on J-Integral and Critical Failure Load of Single-Edge Notched Tensile Aluminium 8011 Alloy Specimens
In this paper, the influence of notch depth-to-width ratios on J-integral and critical load of Aluminium 8011 alloy specimens with U-notch under Mode I loading are studied. Using experiments, for a set of specimens having different notch depth–to–width ratios, J-integral was found and the same was verified using analytical methods. Further, using the results obtained from the experiments, failu...
متن کاملPrediction of Fatigue Life in Notched Specimens Using Multiaxial Fatigue Criteria
In this research, the effects of notch shape on the fatigue strength of 2024-T3 aluminum alloy notched specimens have been studied using experimental and multiaxial fatigue analysis. For this purpose, four set of specimens with different notch shape were prepared and then fatigue tests were carried out at various cyclic longitudinal load levels. Load controlled fatigue tests of mentioned specim...
متن کاملEvaluation of Flow and Fracture Propensity of Notched Steel Plates by Means of a Photoelastic Model
The object of this investigation was to gain a better understanding of the flow and fracture propensity of steel plates in which the Wells-type notch served as the fracture initiator. This type of notch is of importance in experimental investigations of the brittle fracture phenomenon because it successfully initiates low-stress brittle fractures in the wide-plate specimen in which it is used. ...
متن کاملinvestigation of fracture in v-notched brittle polymers under pure shear loading
sudden fracture is one of the major failure modes in brittle materials. plexiglass (polymethyl methacrylate) is a well known brittle polymer, widely used in various industries. many types of notches, particularly v-shaped notches, are sometimes used in the components made of plexiglass. these notches can dramatically decrease the load bearing capacity of components due to the concentration of s...
متن کاملHow Residual Stresses Affect Prediction of Brittle Fracture
It is generally accepted that residual stresses present in welded joints alter the conditions for fracture initiation by contributing to the crack-driving force. In this study, it is shown that weld residual stresses also alter crack-tip constraint, affecting fracture in an additional way. The fracture behavior of two crack geometries, a large pressure shell and a small fracture specimen, both ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Procedia Structural Integrity
سال: 2020
ISSN: 2452-3216
DOI: 10.1016/j.prostr.2020.06.030