Breaking Load Analysis of Wood Plastic Composite Materials with Surface Roughness Variation
نویسندگان
چکیده
منابع مشابه
Effect of Fire Retardants on Surface Roughness and Wettability of Wood Plastic Composite Panels
Surface roughness and wettability of flat-pressed wood plastic composites (WPCs) incorporated with various fire retardants (FRs) (5, 10, or 15% by weight (wt)) at 50 wt-% content of the wood flour (WF) were investigated. The most common FRs, zinc borate (ZB), magnesium hydroxide (MH), and ammonium polyphosphate (APP), were used in the experiments. The WPC panels were made from dry-blended wood ...
متن کاملMachining of Fibre Reinforced Plastic Composite Materials
Fibre reinforced plastic composite materials are difficult to machine because of the anisotropy and inhomogeneity characterizing their microstructure and the abrasiveness of their reinforcement components. During machining, very rapid cutting tool wear development is experienced, and surface integrity damage is often produced in the machined parts. An accurate selection of the proper tool and m...
متن کاملInvestigation of surface roughness of composite fillings.
Various grinders (diamond and carbide burs, and soflex disks) were used in polishing the composite filling surfaces. Polishing was carried out 10 minutes and 14 days after the material polymerization. The ground surface was then observed by a scanning electron microscope and the surface roughness expressed in [xm. Better surface polish and lower de gree of roughness were observed when polishin...
متن کاملFailure Criteria Analysis of Laminate Composite Materials
This paper deals with the development of a numerical simulation methodology for estimating damages in laminate composite materials caused by a low-speed impact. Experimental tests were performed on laminate plates reinforced with woven carbon fibers and epoxy resin. Three thickness plates were evaluated. The impact loads were transversal and punctual. Two lamina failure criteria were evaluated....
متن کاملEffect of Surface Roughness and Materials Composition
In the mouth, biofilm formation occurs on all soft and hard surfaces. Microbial colonization on such surfaces is always preceded by the formation of a pellicle. The physicochemical surface properties of a pellicle are largely dependent on the physical and chemical nature of the underlying surface. Thus, the surface structure and composition of the underlying surface will influence on the initia...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: IOSR Journal of Mechanical and Civil Engineering
سال: 2013
ISSN: 2320-334X,2278-1684
DOI: 10.9790/1684-0562932