Brazing of Titanium with Silver-Base Filler Metals
نویسندگان
چکیده
منابع مشابه
Wettability of Brazing Filler Metals on Copper and Copper Alloys
The possibility of alloying can not be avoided at the interface between molten brazing filler metal and base metal in brazing, so the wettability of brazing filler metal can not be easily explained theoretically. We used the original apparatus for wettability test and investigated the relation between the wettability of brazing filler metals of Ag-P-Cu and Ag-Cu-Zn-Cd systems on copper and the ...
متن کاملبررسی خواص مکانیکی اتصالات در لحیم کاری سخت آلیاژ V4-Al6-Ti به آلیاژ 410 SS در شرایط خلا
In this research, Ti-6Al-4V alloy was brazed with 410 stainless steel by three different filler metals as silver-base, nickel-base, and titanium-base alloys. In order to obtain optimum clearance, brazing was done in three different clearances of 0.02, 0.04 and 0.06 mm. Also, the strength and hardness of the brazing zone were investigated. The results of shear strength showed that the brazed ...
متن کاملVacuum Brazing of Zirconium-Based Alloy and 321 Stainless Steel Using Titanium Based Filler Metal
Both Zirconium-based alloys and 321stainless steel are widely used as engineering alloys due to their good mechanical properties. Conventional fusion welding techniques for Zr alloys and stainless steel are not feasible due to the formation of brittle intermetallic compounds such as (Zr3Fe, ZrFe2 and Zr2Fe) and corrosion cracking. Brazing is one of the most wide...
متن کاملoptimum brazing conditions for joining commercially pure titanium to 304l stainless steel using bag-8 silver filler metal
joining of titanium alloys to other materials especially steels has attracted much attention in recent years due to the exceptional properties of titanium such as excellent corrosion resistance and mechanical properties and its increasing application in various industries. according to the fe-ti binary phase diagram, these two elements do not have complete solubility. this leads to difficulties...
متن کاملLow-Temperature Interface Reaction between Titanium and the Eutectic Silver-Copper Brazing Alloy
Reaction zones formed at 790 °C between solid titanium and liquid Ag-Cu eutectic alloys (pure and Ti-saturated) have been characterized. When pure Ag-Cu eutectic alloy with 40 at.% Cu is used, the interface reaction layer sequence is: αTi / Ti2Cu / TiCu / Ti3Cu4 / TiCu4 / L. Because of the fast dissolution rate of Ti in the alloy, the reaction zone remains very thin (3-6 μm) whatever the reacti...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Welding Society
سال: 1967
ISSN: 0021-4787,1883-7204
DOI: 10.2207/qjjws1943.36.820