Boronizing of equiatomic Fe-Cr binary alloy
نویسندگان
چکیده
منابع مشابه
Dealloying Behaviours of an Equiatomic TiCu Alloy
The crystalline Ti50Cu50 ribbon was prepared by annealing its amorphous counterpart at 773K, 84K higher than its crystallization temperature. An equiatomic TiCu intermetallic phase dominated in the matrix coexisting with trace Ti2Cu phase segregated on the grain boundary. A bi-continuous nanoporous copper from tenths of nanometers to hundredths of nanometers was obtained after dealloying the cr...
متن کاملEvolution of magnetization reversal mechanism in Fe-Cr alloy films
A large thin film sample of FexCr1−x alloy with a composition gradient x=0.38−0.52 has been prepared by co-sputtering to investigate magnetic anisotropy and magnetization effects on reversal mechanisms. The single-phased Fe-Cr films have a bcc structure with 110 preferred orientation. Since the magnetization decreases as the Fe content is decreased and the uniaxial anisotropy energy keeps at al...
متن کاملVibrational properties of alpha- and sigma-phase Fe-Cr alloy.
Experimental and theoretical studies, of the Fe-partial phonon density of states (PDOS) for Fe52.5Cr47.5 alloy having alpha and sigma phases were carried out. The former using the nuclear resonant inelastic x-ray scattering method, and the latter with the direct one. Characteristic features of PDOS, which distinguish one phase from the other, were revealed and successfully reproduced by the the...
متن کاملPhase Separation kinetics in Fe-Cr-Al alloy
9 The α α phase separation kinetics in a commercial Fe-20 wt% Cr-6% Al oxide dispersion-strengthened PM 1
متن کاملJoint properties of cast Fe-Pt magnetic alloy laser-welded to Co-Cr alloy.
This study investigated the joint properties of Fe-Pt alloy laser-welded to Co-Cr alloy. Cast plates (0.5 x 3.0 x 10 mm) were prepared with Fe-Pt and Co-Cr alloys. Fe-Pt plates were butted against Co-Cr plates and laser-welded using Nd:YAG laser. Control and homogeneously welded specimens were also prepared. Laser welding was performed with and without argon shielding. Tensile testing was condu...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Pamukkale University Journal of Engineering Sciences
سال: 2017
ISSN: 1300-7009,2147-5881
DOI: 10.5505/pajes.2017.82956