Bioxidant corrosion behaviour of CoNiCrAlY coated IN738 at 1100 °C
نویسندگان
چکیده
منابع مشابه
Oxidation behaviour of simple and Pt-modified aluminide coatings on IN738 at 1100 °C
The oxidation of both low and high-activity simple and Pt-modified aluminide coatings on nickel base superalloy IN738 has been studied in static air at 1100 OC up to 1000 h. For all coatings oxidation followed a parabolic law up to 400 h. The two Pt-modified coatings showed better protectiveness with lower mass gains and smaller rate constants, especially for long reaction times. The presence o...
متن کاملCorrosion Behaviour of Nickel Coated AISI 316 Stainless Steel as a Function of Annealing Temperature
AISI 316 stainless steels were coated with 250 nm Ni film by electron beam deposition and post-annealed at different temperatures with a nitrogen flow of 600 cm3min-1 nitrogen. The prepared samples were corrosion tested in 1.0 M sulphuric acid solution using potentiodynamic technique. Crystallographic and morphological structure of the samples were analyzedanalysed by X-ray diffraction (XRD) an...
متن کاملThe effect of yttria coatings on the oxidation behaviour of Fe-25Al and Ni-32Al at 1100 and 1200 °C
The influence of Y 2 0 3 coatings on the oxidation behaviour of Fe-25wt%Al and Ni-32wt%Al has been investigated at 1100 and 1200 OC. Samples were sputter coated with 4 nm of Y 2 0 3 and oxidized sequentially in 1602 and Oxide scales have been characterized using SIMS, XPS, SEM, X-ray and electron diffraction. A comparison is made between the growth of oxide on Y203-coated and uncoated alloys. T...
متن کاملA Review of the Fatigue Behaviour of Components Coated with Thin Hard Corrosion-Resistant Coatings
This paper provides a review of the state of the art on the study of the fatigue behaviour of mechanical components coated with thin hard corrosion-resistant coatings such as the physically or chemically vapour deposited ones. Some references address the experimental characterization of the fatigue resistance of coated steel and light alloys. Some coatings have been observed to prove effective ...
متن کاملCorrosion Behaviour of Cardiovascular Stents
Cyclic Potentiodynamic polarization studies were conducted to compare the corrosion resistance of Nitinol cardiovascular stents and stainless steel stents. The tests is to simulate the corrosion behavior of the stents under body condition using Phosphate Buffered Saline (PBS) solution at 37C and following the ASTM F2129-01, Item 2, WK1749, Standard. The results of this study indicate that both ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Corrosion Science
سال: 2019
ISSN: 0010-938X
DOI: 10.1016/j.corsci.2019.02.014