Biological resistance of pine wood treated with nano-sized zinc oxide and zinc borate against brown-rot fungi
نویسندگان
چکیده
منابع مشابه
evaluation of contact angle and leach resistance of beech wood treated with nano-zinc oxide
the objective of this research is characterizing the effect of nano-zinc oxide (nano-zno) dispersions on leach resistance and contact angle of beech wood (fagus orientalis lipsky). the beech wood was cut into standard dimension, and oven dried after treating with nano-zno solution, based on immersion method. three treating nano-zno solution levels: (o, 20000 and 40000 ppm), and two thermal trea...
متن کاملCreep Behavior of Borate-treated Strandboard: Effect of Zinc Borate Retention, Wood Species, and Load Level
Creep performance of zinc borate-treated strandboard from southern pine (Pinus taeda L.) and red oak (Quercus falcata) was investigated at 25°C temperature and 65% relative humidity. It was shown that the borate treatment had some signifi cant effect on creep defl ection of the test panels, and the effect varied with wood species. There was no signifi cant effect of creep loading on residual be...
متن کاملWeatherability and Leach Resistance of Wood Impregnated with Nano-Zinc Oxide
Southern pine specimens vacuum-treated with nano-zinc oxide (nano-ZnO) dispersions were evaluated for leach resistance and UV protection. Virtually, no leaching occurred in any of the nano-ZnO-treated specimens in a laboratory leach test, even at the highest retention of 13 kg/m(3). However, specimens treated with high concentrations of nano-ZnO showed 58-65% chemical depletion after 12 months ...
متن کاملDecay and Mold Resistance of Borate Modified Oriented Strandboard
Decay and mold resistance of zinc borate (ZB) and calcium borate (CB) modified oriented strandboard (OSB) from southern mixed hardwoods and yellow pine was investigated in this study. Tests were done with brown rot, Gloeophyllum trabeum, and white-rot, Trametes versicolar, fungi for 8 and 12 weeks, respectively. Wood species and fungus type had significant influence on the decay resistance. Dec...
متن کاملEffects of Nano-clay on Biological Resistance of Wood- Plastic Composite against Five Wood-deteriorating Fungi
Effects of nano-clay on weight loss of wood-plastic composites (WPC) by five fungi were studied. Nanoclay particles of 20 to 50 nm size were applied at 2, 4, and 6% WPC of 0,90 g/cm3 density. The white-rot fungi Physisporinus vitreus, Pleurotus ostreatus and Trametes versicolor as well as the brown-rot species Antrodia vaillantii and Coniophora puteana were used. Mass loss tests were conducted ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: European Journal of Wood and Wood Products
سال: 2016
ISSN: 0018-3768,1436-736X
DOI: 10.1007/s00107-016-1093-3