Bio-based thermosetting resins composed of cardanol novolac and bismaleimide
نویسندگان
چکیده
منابع مشابه
Synthesis, Characterization, and Application of a Bio-Based Plasticizer for PVC: Epoxidized Acetylation Cardanol
A bio-based plasticizer, epoxidized acetylation cardanol, was synthesized from cardanol, which experienced acetylation reaction and epoxidation reaction. Chemical structure of epoxidized acetylation cardanol was characterized by FT-IR and 1H NMR. Plasticized PVC films (PVC-P) were prepared by casting method with 40%wt of epoxidized acetylation cardanol as a plasticizer. Thermal s...
متن کاملMonitoring the Cure State of Thermosetting Resins by Ultrasound
The propagation of low intensity ultrasound in a curing resin, acting as a high frequency oscillatory excitation, has been recently proposed as an ultrasonic dynamic mechanical analysis (UDMA) for cure monitoring. The technique measures sound velocity and attenuation, which are very sensitive to changes in the viscoelastic characteristics of the curing resin, since the velocity is related to th...
متن کاملThermosetting resins with high fractions of free volume and inherently low dielectric constants.
This work demonstrates a new class of thermosetting resins, based on Meldrum's acid (MA) derivatives, which have high fractions of free volume and inherently low k values of about 2.0 at 1 MHz. Thermal decomposition of the MA groups evolves CO2 and acetone to create air-trapped cavities so as to reduce the dielectric constants.
متن کاملInvestigation of Bio-Composites using Novolac Type Liquefied Wood Resin: Effects of Liquefaction and Fabrication Conditions
Wood liquefaction using an organic solvent and an acid catalyst has long been studied as a novel technique to utilize biomass as an alternative to petroleum-based products. Oxalic acid is a weaker organic acid than a mineral acid and wood liquefaction with oxalic acid as a catalyst will result in a higher amount of wood residue than that with a mineral acid. Yet the wood residue can be used as ...
متن کاملInvestigation of structure property relationships in liquid processible, solvent free, thermally stable bismaleimide-triazine (BT) resins
Three cyanate ester monomer or oligomer species: 2,2-bis(4-cyanatophenyl)propane 1, 1-1-bis(4-cyanatophenyl)ethane (2), and the oligomeric phenolic cyanate (Primaset TM PT30) (3), are blended in various ratios with bis(4-maleimidophenyl)methane, (4), to form binary and ternary mixtures (11 in total) and cured, in the absence of catalysts (3 K/min to 150 °C + 1 hour; 3 K/min to 200 °C + 3 hours)...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Polymer Journal
سال: 2012
ISSN: 0032-3896,1349-0540
DOI: 10.1038/pj.2012.195