Biaxial fatigue tests of notched specimens for AISI 304L stainless steel
نویسندگان
چکیده
منابع مشابه
Biaxial High Cycle Fatigue of a Type 304L Stainless Steel: Cyclic Strains and Crack Initiation Detection by Digital Image Correlation
A series of biaxial High Cycle Fatigue tests at room temperature is performed to build up an extensive and well-documented database. The testing specimen is a maltese cross thinned in its centre with non homogeneous strain/stress fields. The experimental protocol uses exclusively full-field strain measurements. The strains (cyclic and residual) as well as the crack initiation detection are obta...
متن کاملMartensitic Transformation in Ultrafine-Grained Stainless Steel AISI 304L Under Monotonic and Cyclic Loading
The monotonic and cyclic deformation behavior of ultrafine-grained metastable austenitic steel AISI 304L, produced by severe plastic deformation, was investigated. Under monotonic loading, the martensitic phase transformation in the ultrafine-grained state is strongly favored. Under cyclic loading, the martensitic transformation behavior is similar to the coarse-grained condition, but the cycli...
متن کاملEffect of Mean Stress on Fatigue Crack Growth Behavior of Stainless Steel 304L
Stainless steel has been employed in many engineering applications ranging from pharmaceutical equipment to piping in the nuclear reactors and storage to chemical products. In this attempt, simulation of fatigue crack growth based on experimental results of austenitic stainless steel 304L was presented using AFGROW code when NASGRO mode laws adopted. Double through crack at hole specimen is use...
متن کاملRelaxation Peaks of Cold Worked 304l Stainless Steel
In this investigation internal friction of cold worked 304L austenitic stainless steel was measured and the new peaks (PlIP2,P3) were found. The height of those peaks increased with cold work degree. The temperature of the main peak P3 was 33513340K at the frequency of -1,000Hz. The activation energies and frequency factors were obtained from peak shift. The values were 0.4evl 0.4evl 0.6ev and ...
متن کاملEffect of Crystallographic Orientation on the Pitting Corrosion Resistance of Laser Surface Melted AISI 304L Austenitic Stainless Steel
The localized corrosion behavior of laser surface melted 304L austenitic stainless steel was studied by potentiodynamic polarization test. The extent of improvement in corrosion resistance was governed by the preferred orientation and the percentage of delta ferrite present on the surface of the laser melted sample. It was established by orientation imaging microscopy that the highest pitting p...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Frattura ed Integrità Strutturale
سال: 2016
ISSN: 1971-8993
DOI: 10.3221/igf-esis.37.30