Bending Strength and Microstructure of Al<sub>2</sub>O<sub>3</sub>-Y<sub>2</sub>O<sub>3</sub>-MgO and Al<sub>2</sub>O<sub>3</sub>-Y<sub>2</sub>O<sub>3</sub>-ZrO<sub>2</sub>-MgO Composite Ceramics
نویسندگان
چکیده
منابع مشابه
Porous Composite Materials ZrO2(MgO)-MgO for Osteoimplantology
The pore structure and phase composition of ceramic composite material ZrO2(Mg)-MgO at different sintering temperatures were studied. The main mechanical characteristics of the material were determined and it was shown that they are close to the characteristics of natural bone tissues. It was shown that material structure has a positive effect on the pre-osteoblast cells proliferation. In-vitro...
متن کاملSynthesis, Structure, Spectroscopy and Photocatalytic Studies of Nano Multi-Metal Oxide MgO∙Al2O3∙ZnO and MgO∙Al2O3∙ZnO-Curcumin Composite
The mixed metal nanocomposite MgO∙Al2O3∙ZnO has been prepared by coprecipitation method. The product was characterized by XRD. The average particle size was found to be 34.89 nm from XRD data. SEM and SEM-EDS were studied for evaluating surface morphology and elemental composition. The FTIR spectrum of prepared mixed metal nanocomposites MgO∙Al2O3</s...
متن کاملINFLUENCE OF MGO ADDITION ON MICROSTRUCTURE AND PROPERTIES OF REACTION SINTERED ALUMINIUM TITANATE
Effect of MgO addition on reaction sintering of aluminium titanate was investigated using equimolar Al2O3 and TiO2 after firing the samples at 1400 C for four hours. Results showed that MgO addition enhanced the sintering process by magnesium aluminates formation, which led to lower porosity and improved densification of the samples. Physical and mechanical properties showed that samples contai...
متن کاملEffect of Nano-Sized Fe2O3 on Microstructure and Hydration Resistance of MgO-CaO Refractories
In this work the effect of Nano-sized Fe2O3 on microstructure and hydration resistance of MgO-CaO refractories with 35 wt% CaO was investigated. MgO-CaO refractories with 35 wt% CaO content was prepared by using dolomite and magnesite calcined as starting materials and Nano-sized Fe2O3 (2,4, 6 and 8 wt%) as an additive. Samples were pressed into ...
متن کاملTemplate synthesis and characteristics of nanoparticle MgO
Oxide nanoparticles can exhibit unique physical and chemical properties due to their limited size and a high density of corner or edge surface sites. In this study, MgO nanoparticle was synthesized using Mg(CH3COO)2 and hexamethylenetetramine as starting materials. The structure and optical properties of these particles are investigated by using X-ray diffraction (XRD), sc...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Ceramic Society of Japan
سال: 1992
ISSN: 0914-5400,1882-1022
DOI: 10.2109/jcersj.100.608