Bending Fatigue Behaviour and Fatigue Endurance Limit Prediction of 20Cr2Ni4A Gear Steel after the Ultrasonic Surface Rolling Process
نویسندگان
چکیده
منابع مشابه
Interior Fracture Mechanism Analysis and Fatigue Life Prediction of Surface-Hardened Gear Steel under Axial Loading
The interior defect-induced fracture of surface-hardened metallic materials in the long life region has become a key issue on engineering design. In the present study, the axial loading test with fully reversed condition was performed to examine the fatigue property of a surface-carburized low alloy gear steel in the long life region. Results show that this steel represents the duplex S-N (stre...
متن کاملAssessment of different methods for fatigue life prediction of steel in rotating bending and axial loading
Generally, fatigue failure in an element happens at the notch on a surface where the stress level rises because of the stress concentration effect. The present paper investigates the effect of a notch on the fatigue life of the HSLA100 (high strength low alloy) steel which is widely applicable in the marine industry. Tensile test was conducted on specimens and mechanical properties were obtain...
متن کاملBending Fatigue Failures in Valve Steel
In the present paper the effect of defects (viz. pits, gouges and oxide inclusions) will be reported. Although certain defects were uniformly distributed over the specimen surface, the majority of all fractures started in the edge region. An explanation to this behaviour is presented in terms of stress enhancement in the edge regions due to edge deflections.
متن کاملImpact Fatigue Behaviour of Flapper Valve Steel
The purpose of this study is to discuss the impact fatigue failure mechanism of a suction valve that involves the fracture with fragments torn off from the edge or surface. The shape and dimensions of the test specimen and stopper were made the same as those of the suction valve and stopper in an actual compressor. The specimen was operated by short-duration compressed air pulses, and struck ag...
متن کاملassessment of different methods for fatigue life prediction of steel in rotating bending and axial loading
generally, fatigue failure in an element happens at the notch on a surface where the stress level rises because of the stress concentration effect. the present paper investigates the effect of a notch on the fatigue life of the hsla100 (high strength low alloy) steel which is widely applicable in the marine industry. tensile test was conducted on specimens and mechanical properties were obtain...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials
سال: 2021
ISSN: 1996-1944
DOI: 10.3390/ma14102516