Bearing Strength and Failure Mechanisms of Riveted Woven Carbon Composite Joints
نویسندگان
چکیده
This research aimed to determine riveted carbon/epoxy composites’ mechanical performance when fabricated by resin transfer molding (RTM). As this manufacturing process is gaining importance in the aeronautics and automotive industries, assembly methods their reliability must be studied terms of airworthiness transportation implementation. The study case resumes determination bearing strength RTM-woven carbon composites for different rivet joint diameters (1/8, 5/32 3/16 in). shear was obtained following ASTM D5961 instructions, post-failure analysis carried out a computerized tomography scan. A residual curve provided with results infer as function width-to-diameter ratio. discussion fracture mechanism tensile assess understanding woven composites.
منابع مشابه
A review on stress distribution, strength and failure of bolted composite joints
In this study, analytical models considering different material and geometry for both single and double-lap bolted joints were reviewed for better understand how to select the proper model for a particular application. The survey indicades that the analytic models selected for the adhesively single or double bolted lap joints, as well as T, scarf, and stepped joints, with linear material pr...
متن کاملResidual Strength Analyses of Riveted Lap-Splice Joints
Aging aircraft may develop multiple-site damage (MSD) that can reduce the structural integrity of fuselage structures. The existence of small cracks emanating from adjacent rivet holes in a fuselage lap-splice joint is of major concern. Small collinear cracks greatly reduce the residual strength of a panel with a lead crack. Recent studies predicting the residual strength of flat and curvilinea...
متن کاملStrength of Composite Scarf Joints
In recent years, large composite structures have been used increasingly in the aerospace and naval industries. Such a large composite structure is mostly fabricated using the scarf joining technique so that multiple substructures can be connected together. Figure 1 shows three commonly used scarf joint configuration. Among the three, the step/overlap joint is considered as the strongest because...
متن کاملDesigning for Manufacturability in Riveted Joints
The study of human experts in the areas of design and manufacturing has lead to two hypotheses concerning the problem solving methods which these engineers utilize to attack difficult problems. The basis of both hypotheses is a modular approach to problem solving. One hypothesis addresses the nature of the modules utilized while the other hypothesis deals with the organization of the modules. A...
متن کاملCompressive response of a 3D non-woven carbon-fibre composite
The compressive response of a three-dimensional (3D) non-interlaced composite comprising three orthogonal sets of carbon fibre tows within an epoxy matrix is analysed. First, the compressive response is measured in three orthogonal directions and the deformation/failure modes analysed by a combination of X-ray tomography and optical microscopy. In contrast to traditional unidirectional and two-...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Aerospace
سال: 2021
ISSN: ['2226-4310']
DOI: https://doi.org/10.3390/aerospace8040105