Ball milling nanocrystallization of arc-melted and melt-spun Fe78Co5Nb3Zr3B5Ge5Cu1alloy: microstructure and magnetic properties

نویسندگان
چکیده

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Magnetic properties and synthesis conditions of Nd2Fe23B3 melt-spun alloy

The formation of amorphous and crystalline state of the Nd2Fe23B3 alloy from melt-spun ribbon is presented. The synthesis conditions are investigated combining DSC, X-ray diffraction and thermomagnetic analysis. The thermomagnetic analysis is found to be very useful to optimize the synthesis process. Comparison of these results enables to discuss the thermal stability of both the amorphous and ...

متن کامل

The Structure and Magnetic Properties of Co77Zr18W5 Melt-Spun Ribbons

Based on X-ray diffraction, microscopic and magnetic analysis, the structure and magnetic properties of Co77Zr18W5 melt-spun ribbons were studied in this paper. A new element to stabilize the metastable Co5Zr phase was found and the coercivity observed in Co-Zr alloys can be obviously enhanced by proper tungsten substitution. The Curie temperature of Co77Zr18W5 ribbons is 475 ̊C which suggests t...

متن کامل

Hard magnetic properties of melt-spun Mn-Al-C alloys

Structural and magnetic characterization of Mnx−yAl100−x−yC2y (x = {50, 55}; y = {0, 1}) melt-spun ribbons is reported. To obtain the metastable ferromagnetic τ-phase, rapidly solidified alloys were annealed either in a vacuum furnace at 823 K or directly in the vibrating sample magnetometer under applied magnetic field. Optimal magnetic properties were demonstrated by Mn54Al44C2 samples proved...

متن کامل

Microstructure and magnetic domain structure of boron - enriched Nd 2 ( FeCo ) 14 B melt - spun ribbons

Heat treated melt-spun ribbons of (Nd La) Fe Co Nb B have been studied systematically by supercon-ducting quantum interference device (SQUID) magnetometry, conventional transmission electron microscopy (CTEM) and Lorentz transmission electron microscopy (LTEM). The sample's microstructure grew from an amorphous state through a partially crystallized state at 6503C, and "nally to a fully crystal...

متن کامل

Magnetic properties of B2-structure CoZr upon ball milling

Magnetization measurements of B2-structure CoZr after high-energy ball milling have been performed at 4.2 K in the Amsterdam High Field Installation in fields up to 35 T. It turns out that the magnetic behavior of the ball-milled CoZr is drastically different from the unmilled sample. The magnetization at 21 T increases abruptly in the early state of milling due to the introduction of anti-site...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: Philosophical Magazine

سال: 2006

ISSN: 1478-6435,1478-6443

DOI: 10.1080/14786430500300074