B8-Type Solid Solutions of Manganese Antimonide and Cu, Zn, Al, or~Si

ANELASTIC EFFECTS IN SINGLE CRYSTALS OF -Cu-Zn AND -Cu-Zn-Al ALLOYS

Formation of a solid solution through accumulative roll bonding (ARB) and post-heat treatment of multilayered Cu/Zn/Al

In the present study, the capability of accumulative roll bonding (ARB) and subsequent heat-treatment to fabricate solid solution from a multilayered Cu/Zn/Al was investigated. Two post-heat treatment (one-step and two-step) routes were proposed. In the first, the ARB processed material was heated to 800 C for 5:30 hours and allowed to cool slowly in a furnace (one-step route). In the second (t...

STRUCTURE OF STABLE INTERMETALLIC COMPOUNDS OF THE Al-Li-Cu-(Mg) AND Al-Li-Zn-(Cu) SYSTEMS

The results of a thorough structural study of crystalline intermetallic compounds within the Al-Li-(Cu,Mg,Zn) system are given. Characteristic morphologies of these ternary or quaternary phases are exhibited by concentrated alloys or large single crystals. Typical X-ray powder diffraction data, selected area electron diffraction patterns and high resolution electron microscopy images are shown,...

the investigation of the relationship between type a and type b personalities and quality of translation

چکیده ندارد.

Shape Memory Properties in Cu-Zn-Al Alloy

In this research a Cu-Zn-Al alloy is produced by melting the raw materials in an electric resistance furnace and then pouring it into a steel mould. The optimum way to achieve the final analysis in the hypo-eutectoid range is determined and the influence of the alloying element, Ti on the grain size and the shape memory properties of the samples are investigated. Solution treatment (done at 850...