Austenite Grain Refinement and Superplasticity in HSLA Steel
نویسندگان
چکیده
منابع مشابه
Superplasticity of Annealed H13 Steel
H13 steel is a widely used hot work die material. A new type of hot working method is imperative to develop complex and precise dies. In this paper, the heat treatment of H13 steel (AISI) was carried out by annealing, the final structure is a point or spherical pearlite, and the grain size is about 30-40 μm. The tensile properties of the annealed microstructure were investigated at 650, 750, an...
متن کاملThe Effect of Hot Deformation Parameters on Grain Size Refinement in a Martensitic Stainless Steel
The grain size refinement of AISI 422 martensitic stainless steel in the temperature range of 950-1150 ºC was investigated by hot deformation tests. The deformed specimens were held at deformation temperature with delay times of 5 to 300s after achieving a strain of 0.3. The austenite grains exhibit a considerable growth at temperature higher than 1050˚C, while the grain coarsening is negligibl...
متن کاملRefinement of retained austenite in super-bainitic steel by a deep cryogenic treatment
1) Hubei Collaborative Innovation Center for Advanced Steels, International Research Institute for Steel Technology, Wuhan University of Science and Technology, Wuhan, 430081 China. 2) Institute for Frontier Materials, Deakin University, Geelong, Victoria, 3226 Australia. 3) Department of Engineering and Innovation, The Open University, Walton Hall, Milton Keynes, MK7 6AA UK. 4) Department of M...
متن کاملThe Effect of Precipitate Evolution on Austenite Grain Growth in RAFM Steel
To study the effects of various types of precipitates and precipitate evolution behavior on austenite (size and phase fraction) in reduced activation ferritic/martensitic (RAFM) steel, RAFM steel was heated to various austenitizing temperatures. The microstructures of specimens were observed using optical microscopy (OM) and transmission electron microscopy (TEM). The results indicate that the ...
متن کاملGrain Refinement of Dual Phase Steel via Tempering of Cold-Rolled Martensite
A microstructure consisting of ultrafine grained (UFG) ferrite with average grain size of ~ 0.7 µm and dispersed nano-sized carbides was produced by cold-rolling and tempering of the martensite starting microstructure in a low carbon steel. Subsequently, fine grained dual phase (DP) steel consisting of equiaxed ferrite grains with average size of ~ 5 µm and martensite islands with average size ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Tetsu-to-Hagane
سال: 1985
ISSN: 0021-1575,1883-2954
DOI: 10.2355/tetsutohagane1955.71.2_228