Atomic Ordering and Magnetic Hardening in Pt-Pd-Fe Alloys
نویسندگان
چکیده
منابع مشابه
MAGNETIC STATES INSTABILITY OF Pt-Fe ALLOYS
Neutron-diffraction measurements have been used to 'determine the temperature and composition dependences of the ordered single crystals of Pt-Fe alloys containing 32, 30.5 and 28 at% of iron. A qualitative model for the complex antiferromagnetic ordering in the system based on the experimental data and band structure calculations has been proposed. The ordered Pt-Fe alloys with more than 36 at...
متن کاملATOMIC AND MAGNETIC SRO IN Fe-Mn-Si ALLOYS
Neutron diffuse scattering and saturation magnetization experiments have been made on single crystals specimens of Fe3-,MnCSi with c = 0.164 and 0.284 at room temperature. Atomic clustering of Mn atoms on the B sublattice has been revealed. A model of magnetic moment distribution around Mn impurities has been developed and fitted to the experimental magnetic diffuse cross sections. RRsults obta...
متن کاملSome magnetic properties of platinum-rich Pt-Fe alloys
2014 Measurements of magnetic susceptibility and spontaneous magnetization on face centred cubic platinum-iron alloys having compositions around Pt3Fe and also on alloys with lower iron contents, are reported. In the Pt3Fe superlattice region the alloys appear to be antiferromagnetic when ordered and ferromagnetic when disordered. The more dilute alloys are ferromagnetic, even down to 2 at. % o...
متن کاملOrdering tendencies in the binary alloys of Rh, Pd, Ir, and Pt: Density functional calculations
Brian Kolb,1 Stefan Müller,2 David B. Botts,3 and Gus L. W. Hart1,4,* 1Department of Physics and Astronomy, Northern Arizona University, Flagstaff, Arizona 86011, USA 2Lehrstuhl für Festköperphysik, Universität Erlangen-Nürnberg, D-91058 Erlangen, Germany 3Department of Chemistry, Northern Arizona University, Flagstaff, Arizona 86011, USA 4Department of Physics and Astronomy, Brigham Young Univ...
متن کاملMartensitic transformation in Pd-rich Fe–Pd–Pt alloy
The fct martensite morphology and the martensite transformation temperatures are examined for Pd-rich Fe–Pd–Pt alloys, which have the composition of Fe–(xPdyPt)xþy1⁄430 at:%. The replacement of Pd with Pt content causes solution hardening. The shape memory effects are investigated below the Af temperatures. Above the Af temperatures, the stress induced martensite in several grains completely di...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Institute of Metals and Materials
سال: 1972
ISSN: 0021-4876,1880-6880
DOI: 10.2320/jinstmet1952.36.1_53