Artificial pinning centers using the barrier layer of ordered nanoporous alumina templates
نویسندگان
چکیده
منابع مشابه
Ordered Nanoporous Alumina Membranes Formed in Oxalic/Phosphoric Acid Using Hard Anodization
Highly self-ordered alumina nanopore arrays were fabricated using hard anodization technique in different mixtures of oxalic/phosphoric acid. The phosphoric acid concentration was varied from 0.05 to 0.3 M while the oxalic acid concentration was changed between 0.3 and 0.4 M. The self ordered nanoporous arrays were obtained in anodization voltage changing from 130 to 200 V. The interpore distan...
متن کاملOrdered Nanomaterial Thin Films via Supported Anodized Alumina Templates
*Correspondence: Mohammed Es-Souni , Institute for Materials and Surface Technology, University of Applied Sciences, Grenzstrasse 3, Kiel, Germany e-mail: [email protected] Supported anodized alumina template films with highly ordered porosity are best suited for fabricating large-area ordered nanostructures with tunable dimensions and aspect ratios. In this paper, we first discuss important issues...
متن کاملFabrication of Ordered Arrays of Nanodots Using Porous Alumina Thin Film Templates
Nanostructured materials have attracted much research over the recent years, as they provide the critical building blocks for the booming of nanoscience and nanotechnology. Nanostructures have novel properties due to the interplay between the size confinement of electrons in small structures and proximity effects. This is relevant for example in device miniaturization towards the Tbit/in record...
متن کاملFabrication of nanomaterials using porous alumina templates
Nanofabrication by self-organization methods has attracted much attention owing to the fact that it enables mass production without the use of expensive lithographical tools, such as an electron beam exposure system. Porous alumina can be fabricated electrochemically through anodic oxidation of aluminum by means of such a self-organization method, yielding highly ordered arrays of nanoholes sev...
متن کاملRoom Temperature Ammonia and Humidity Sensing Using Highly Ordered Nanoporous Alumina Films
The effect of pore size and uniformity on the response of nanoporous alumina, formed on aluminum thick films through an anodization process, to ammonia and humidity at room temperature is reported. Pore sizes examined range from 13 nm to 48 nm, with pore size standard deviations ranging from 2.6 nm to 7.8 nm. The response of the material to ammonia and humidity is a strong function of pore size...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Physics: Conference Series
سال: 2009
ISSN: 1742-6596
DOI: 10.1088/1742-6596/153/1/012013