Morphology-controlled synthesis of barium titanate nanostructures.
This study reports the synthesis of morphology-controlled BaTiO(3) nanostructures such as spherical, cube-shaped and rod-shaped BaTiO(3) using a molten-salt synthesis method. This method synthesized products from a reaction of BaO/BaCO(3) and TiO(2) with a eutectic mixture of NaCl-KCl flux at 700 degrees C for 1 h. The experiment used powder X-ray diffraction, field emission scanning electron m...
متن کاملSynthesis of Barium-zinc-titanate Ceramics
Mixtures of BaCO3, ZnO and TiO2 powders, with molar ratio of 1:2:4, were mechanically activated for 20, 40 and minutes in a planetary ball mill. The resulting powders were compacted into pellets and isothermally sintered at 1250 °C for 2h with a heating rate of 10 °C/min. X-ray diffraction analysis of obtained powders and sintered samples was performed in order to investigate changes of the pha...
متن کاملRemoval of Barium Ions from Aqueous Solutions by Barium Titanate Using Radiotracer Technique:
The adsorption of barium ions on barium titanate in an aqueous solution was studied by means of batch technique as a function of Ba(II) concentration, temperature and solution pH using Ba-140 as radiotracer. The results show that adsorption is essentially complete in ca 180min and the steady state values of adsorption at various concentrations agree well with the classical Freundlich isotherm a...
متن کاملDc and Ac Electrical Properties of Ptc Barium Titanate Ceramics
The dc and ac electrical properties of PTC barium titanate ceramics were measured in the temperature range from 30 to 450°C. The Heywang's model alone is not sufficient to perform a quantitative analysis of the results. The heterogeneity of the system is taken into account.
متن کاملSynthesis of single-crystalline perovskite nanorods composed of barium titanate and strontium titanate.
We report the solution-based synthesis of single-crystalline nanorods composed of barium titanate (BaTiO3) and strontium titanate (SrTiO3), which yields well-isolated nanorods with diameters ranging from 5 to 60 nm and lengths reaching up to >10 mum. Electron microscopy and diffraction measurements show that these nanorods are composed of single-crystalline cubic perovskite BaTiO3 and SrTiO3 wi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: NIPPON KAGAKU KAISHI
سال: 1974
ISSN: 2185-0925,0369-4577
DOI: 10.1246/nikkashi.1974.1155