Application of intermetallic compound precipitates for iron and steel.

Superstrength of nanograined steel with nanoscale intermetallic precipitates transformed from shock-compressed martensitic steel

An increasing number of industrial applications need superstrength steels. It is known that refined grains and nanoscale precipitates can increase strength. The hardest martensitic steel reported to date is C0.8 steel, whose nanohardness can reach 11.9 GPa through incremental interstitial solid solution strengthening. Here we report a nanograined (NG) steel dispersed with nanoscale precipitates...

ANALYTICAL DATA FOR NiO REDUCTION AND Al3Ni2 INTERMETALLIC COMPOUND FORMATION

In this research, the nickel oxide was dissolved in cryolite at temperatures of 880, 940 and 1000°C. In order to reduce the nickel oxide, aluminum was added to the salt. Simultaneously the nickel oxide was reduced and Al3Ni2 intermetallic compound was formed. In the duration intervals of 2.5-40 minutes samples of the salt and metallic phases were taken. The variation of the nickel content in me...

Control of Formation of Intermetallic Compound in Dissimilar Joints Aluminum-steel

The elimination of the FexAly type phases was considered the solution to low ductility presented in aluminum-steel welded joints. Recently, the researches do not seek the suppression but the control of the thickness of these compounds. In this work, Al-Fe joints were manufactured by solid state and fusion welding, looking for controlling the formation of intermetallic comp...

Enhanced iron magnetic moment in the ThFe11C2 intermetallic compound

Tribological Behaviour of Fe-Al Intermetallic Compound Coated Carbon Tool Steel

The use of Fe-Al intermetallic compound coatings has been investigated in order to improve the tribological behaviour of carbon tool steel. The coatings were formed by a pack cementation process and subsequently diffusion annealing at 900˚C in an argon controlled atmosphere. The optimum diffusion time was selected on the basis of optimum thickness and tribological behaviour. The microstructure...