Anisotropy Distribution and Magnetoimpedance in Stress Annealed Amorphous Ribbons

Longitudinally driven giant magnetoimpedance effect in stress-annealed Fe-based nanocrystalline ribbons

A high-frequency longitudinally driven giant magnetoimpedance ~GMI! effect has been measured in stress-annealed Fe73Cu1Nb1.5V2Si13.5B9 nanocrystalline ribbons. Based on how the impedance phase varies with the external magnetic field, it becomes clear that the imaginary part of the complex permeability, m9, which is related to magnetic losses, plays an important role in the high-frequency longit...

Induced anisotropies in ferromagnetic amorphous ribbons locally annealed by laser.

The origin of anisotropy induced by local laser annealing has been studied in amorphous ferromagnetic materials with different magnetostriction constants. The results have been explained using a theoretical model based on the assumption that the origin of the induced anisotropies are internal stresses produced by inhomogeneous heat flows during the local laser annealing. The induced anisotropie...

Nanocrystallization in Co67Cr7Fe4Si8B14 Amorphous Alloy Ribbons

The nanocrystallization of Co67Fe4Cr7Si8B14 amorphous ribbons which prepared by planar flow melt spinning process (PFMS) was investigated. Crystallization of the ribbons was studied by differential thermal analysis (DTA), X-ray diffraction (XRD) and transmission electron microscopy (TEM). The DTA result of amorphous ribbon at heating rate of 10˚C/min showedoccurrence of phase transitions in two...

Giant magnetoimpedance and field sensitivity in amorphous and nanocrystalline (Co1â‹TMxFex)89Zr7B4 (xâ•›=â•›0, 0.025, 0.05, 0.1) ribbons

Temperature stability of field induced anisotropy in soft ferromagnetic Fe,Co-based amorphous and nanocomposite ribbons

The temperature stability of field induced uniaxial anisotropy KU was investigated by thermomagnetic treatments of Co1−xFex 89Zr7B4 amorphous ribbons after field annealing below and above the crystallization temperature. We conclude: 1 Field annealing treatments are necessary to properly investigate the temperature stability of KU, 2 KU of field crystallized alloys exhibit improved temperature ...