Anisotropic dislocation nucleation in ZrB2 grains and deformation behaviour of constituents of ZrB2-SiC and ZrB2-B4C composites during nanoindentation
نویسندگان
چکیده
منابع مشابه
Co-Dispersion Behavior of ZrB2–SiC–B4C–C Powders with Polyethyleneimine
The aqueous dispersion behavior of ZrB₂, SiC powders with B₄C and C as sintering aids was investigated. Well co-dispersed suspension can be obtained in acidic solutions in presence of polyethyleneimine (PEI). The adsorption of PEI on the powder surface was measured by thermal gravimetric (TG) analysis. Rheological measurements displayed the effect of dispersant on the flow behavior of as-prepar...
متن کاملEffect of Repeated Thermal Shock on Mechanical Properties of ZrB2-SiC-BN Ceramic Composites
ZrB2-20 vol.% SiC-10 vol.% h-BN (particles) ceramic composites (ZSB) were fabricated by hot pressing under inert gas protected. ZSB samples with mean size 75 × 55 × 40 mm(3) were heated using current heating method and then cooled down to low temperature by circulating water. ZSB samples repeatedly went through thermal shock with 10-50 times under various conditions, respectively. Diverse effec...
متن کاملThe ZrO2 Formation in ZrB2/SiC Composite Irradiated by Laser
In order to clearly understand the details of ZrO₂ formation during ablation, high intensity continuous laser was chosen to irradiate ZrB₂/SiC. The results reveal that there are two different modes of ZrO₂ formation depending on whether liquid SiO₂ is present. When liquid SiO₂ is present, ZrO₂ generated by the oxidation of ZrB₂ is firstly dissolved into SiO₂. Then, ZrO₂ will precipitate again, ...
متن کاملThermal Shock Properties of ZrB2-SiCp-Graphite and ZrB2-SiCp-AlN Ceramic Matrix Composite Material
Thermal shock property of the material can be improved by improving fracture property of the material. In this paper, factors affecting fracture property have been studied and the effect of residual stress, microstructure, strain rate and stress concentration on fracture property of material has been analyzed, which may provide help for improving thermal shock property of material. Thermal shoc...
متن کاملThermochemical and Mechanical Stabilities of the Oxide Scale of ZrB2+SiC and Oxygen Transport Mecha
Refractory diboride with silicon carbide additive has a unique oxide scale microstructure with two condensed oxide phases (solid+liquid), and demonstrates oxidation resistance superior to either monolithic diboride or silicon carbide. We rationalize that this is because the silica-rich liquid phase can retreat outward to remove the high SiO gas volatility region, while still holding onto the zi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the European Ceramic Society
سال: 2020
ISSN: 0955-2219
DOI: 10.1016/j.jeurceramsoc.2019.12.024