ANALYSIS OF MICROSTRUCTURE AND HARDNESS OF WELDED JOINTS OF DISSIMILAR STEEL OF AISI 1018 - AISI 304
نویسندگان
چکیده
منابع مشابه
Microstructure and mechanical properties evaluation of diffusion bonded joints of titanium to AISI 304 austenitic stainless steel
In this study, diffusion bonding between titanium and AISI 304 austenitic stainless steel by Ag interlayer was investigated. In order to carry out this research, samples prepared after surface preparation were placed inside the fixture and placed at the temperatures of 750,800 and 850 °C in the 30,60 and 90 min in the furnace under argon protective gas. The phase transformation and microstructu...
متن کاملMechanical Characterization of Friction Welded AISI 304 Steels
There are many industries where austenitic stainless steel needs to be welded specially in power generation industries. Unfortunately the austenitic stainless welding has several fabrication and metallurgical drawbacks when welded by using conventional fusion welding methods, which can often leads to in-service failure. The most pronounced fabrication faults are hot cracks due to inadvertent us...
متن کاملMicrostructure and mechanical properties evaluation of diffusion bonded joints of titanium to AISI 304 austenitic stainless steel
In this study, diffusion bonding between titanium and AISI 304 austenitic stainless steel by Ag interlayer was investigated. In order to carry out this research, samples prepared after surface preparation were placed inside the fixture and placed at the temperatures of 750,800 and 850 °C in the 30,60 and 90 min in the furnace under argon protective gas. The phase transformation and microstructu...
متن کاملWear Analysis during End Milling AISI 1018 Steel Using Microlubrication
Microlubrication minimizes the exposure of metal working fluids (MWFs) leading to an economical, safer and healthy workplace environment. In this study vegetable based lubricant is used to conduct wear analysis during end milling AISI 1018 steel using microlubrication. Solid carbide cutting tool was used with varying cutting speed and feed rate having a constant depth of cut. A full factorial e...
متن کاملMicrostructural Properties of Semisolid Welded Joints for AISI D 2 Tool Steel
The aim of this study is to investigate experimentally the microstructural evolution of the joints using ledeburitic AISI D2 Tool Steel parts. The application of a new process of the semisolid joining of two parts of AISI D2 cold-work tool steel is proposed using a partial remelting method. Samples were heated in an argon atmosphere up to 1300°C and held for 10 minutes. Metallographic analyses ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Jurnal Sains Materi Indonesia
سال: 2019
ISSN: 2614-087X,1411-1098
DOI: 10.17146/jsmi.2019.20.4.5280