An Anomaly in Young's Modulus of High-manganese Austenitic Steel in Cold-worked States
نویسندگان
چکیده
منابع مشابه
Heat treatment of high manganese type X57MnAl27-5 austenitic steel
In the paper, the influence of heat treatment parameters on microstructure and mechanical properties of high manganese type X57MnAl27-5 austenitic steel was investigated. The as-forged bar with diameter of 15 mm were underwent a saturation process at six different temperatures. The microstructural changes of austenite and the influence of heat treatment on the mechanical properties were conside...
متن کاملEffect of annealing process on microstructure and mechanical properties of high manganese austenitic TWIP steel
In the present study, the influence of annealing temperature on mechanical properties and the microstructure of a high manganese austenitic steel (Fe-30Mn-4Al-4Si-0.5C) was investigated. X-ray diffractometry, optical and scanning electron microscopy, hardness and tensile tests were used to analyze the relationship between mechanical properties and microstructure after annealing process. The res...
متن کاملMulti-Scale Modeling of the Impact Response of a Strain-Rate Sensitive High-Manganese Austenitic Steel
*Correspondence: Demircan Canadinc, Rumeli Feneri Yolu, Sariyer, Istanbul, Turkey e-mail: [email protected] A multi-scale modeling approach was applied to predict the impact response of a strain rate sensitive high-manganese austenitic steel. The roles of texture, geometry, and strain rate sensitivity were successfully taken into account all at once by coupling crystal plasticity and finite e...
متن کاملTWIP-effect and thermo-mechanical treatment of a stable high-manganese austenitic stainless steel
Austenitic carbon steels that exhibit excellent mechanical properties due to the twinning-induced plasticity effect have been studied extensively. On the other hand, austenitic stainless steels usually achieve good strength and ductility via transformation-induced plasticity. However, relying on martensite transformation for strength may cause problems such as delayed cracking. Therefore, the t...
متن کاملRelaxation Peaks of Cold Worked 304l Stainless Steel
In this investigation internal friction of cold worked 304L austenitic stainless steel was measured and the new peaks (PlIP2,P3) were found. The height of those peaks increased with cold work degree. The temperature of the main peak P3 was 33513340K at the frequency of -1,000Hz. The activation energies and frequency factors were obtained from peak shift. The values were 0.4evl 0.4evl 0.6ev and ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Tetsu-to-Hagane
سال: 1998
ISSN: 0021-1575,1883-2954
DOI: 10.2355/tetsutohagane1955.84.7_522