Crystallization Kinetics Study in Al87Ni10La3 Amorphous Alloy
In this study, the crystallization behavior of melt-spun Al87Ni10La3 amorphous phase was investigated by using X-ray diffraction and non-isothermal differential thermal analysis techniques. The results demonstrated that the amorphous phase exhibited two-stage crystallization on heating, i.e., at first step the amorphous phase transforms into α-Al phase and at second step Al11La3 and Al3Ni inter...
متن کاملNanocrystallization in Co67Cr7Fe4Si8B14 Amorphous Alloy Ribbons
The nanocrystallization of Co67Fe4Cr7Si8B14 amorphous ribbons which prepared by planar flow melt spinning process (PFMS) was investigated. Crystallization of the ribbons was studied by differential thermal analysis (DTA), X-ray diffraction (XRD) and transmission electron microscopy (TEM). The DTA result of amorphous ribbon at heating rate of 10˚C/min showedoccurrence of phase transitions in two...
متن کاملnanocrystallization in co67cr7fe4si8b14 amorphous alloy ribbons
the nanocrystallization of co67fe4cr7si8b14 amorphous ribbons which prepared by planar flow melt spinning process (pfms) was investigated. crystallization of the ribbons was studied by differential thermal analysis (dta), x-ray diffraction (xrd) and transmission electron microscopy (tem). the dta result of amorphous ribbon at heating rate of 10˚c/min showedoccurrence of phase transitions in two...
متن کاملSuperparamagnetic behaviour of amorphous Hf57Fe43 alloy
The magnetization processes in binary magnetic/nonmagnetic amorphous alloy Hf57Fe43 are investigated by the detailed measurements including magnetic hysteresis loops, dependence of magnetic moment on temperature and relaxation of magnetic moment. The blocking of magnetization at lower temperatures is accompanied by the slow relaxation of magnetic moment and magnetic hysteresis loops. All of obs...
متن کاملImprinting bulk amorphous alloy at room temperature
We present investigations on the plastic deformation behavior of a brittle bulk amorphous alloy by simple uniaxial compressive loading at room temperature. A patterning is possible by cold-plastic forming of the typically brittle Hf-based bulk amorphous alloy through controlling homogenous flow without the need for thermal energy or shaping at elevated temperatures. The experimental evidence su...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: ISIJ International
سال: 1989
ISSN: 0915-1559
DOI: 10.2355/isijinternational.29.539