Precipitation evolution in Al–Zr and Al–Zr–Ti alloys during aging at 450–600 C
The transformation of Al3Zr (L12) and Al3(Zr1 xTix) (L12) precipitates to their respective equilibrium D023 structures is investigated in conventionally solidified Al–0.1Zr and Al–0.1Zr–0.1Ti (at.%) alloys aged isothermally at 500 C or aged isochronally in the range 300– 600 C. Titanium additions delay neither coarsening of the metastable L12 precipitates nor their transformation to the D023 st...
متن کاملReactivity of the dinuclear fulvalene cyclopentadienyl zirconium cationic species [{Zr(
The dinuclear cationic zirconium compound [{Zr( -C5H5)}2( -CH2)( -Cl)( -C5H4-C5H4)][BMe(C6F5)3] 1 reacts in dichloromethane at −78 °C with three equivalents of RNC (R= Bu, 2,6-Me2C6H3) via insertion into the Zr-methylene bond to give the new zirconium cationic species [{Zr( -C5H5)}2(Cl)(CNBu){ -[ -CN(Bu)-CH2-CN(Bu)}( -C5H4-C5H4)][BMe(C6F5)3] 2 and [{Zr( -C5H5)}2(Cl){CN(2,6-Me2C6H3)}[ -{CN(2,6-M...
متن کاملPrecipitation hardening in dilute Al–Zr alloys
The aim of this study was to investigate the effect of solute content (hipoperitectic Al–0.22 wt.%Zr and hiperperitectic Al–0.32 wt.%Zr) on the precipitation hardening and microstructural evolution of dilute Al–Zr alloys isothermally aged. The materials were conventionally cast in a muffle furnace, solidified in a water-cooled Cu mold and subsequently heat-treated at the temperature of 650 K (3...
متن کاملPrecipitation evolution in Al–Zr and Al–Zr–Ti alloys during isothermal aging at 375–425 C
Formation of Al3Zr or Al3(Zr1 x Tix) precipitates with a metastable L12 structure was investigated in conventionally solidified A1–0.1 Zr, Al–0.2 Zr, Al–0.1 Zr–0.1 Ti, and Al–0.2 Zr–0.2 Ti (at.%) alloys aged isothermally at 375, 400, or 425 C. Pronounced hardening results from nanometer-scale, spheroidal Al3Zr or Al3(Zr1 xTix) (L12) precipitates within solute-enriched dendrites. Interdendritic ...
متن کاملSpontaneous nano-clustering of ZrO2 in atomic layer deposited LayZr1-yOx thin films: Part 1 – Material characterization
During atomic layer deposition (ALD) of uniform LayZr1-yOx thin films, spontaneous segregation of ZrO2 nanocrystals takes place that are embedded in an amorphous La2O3 matrix. This occurs if the Zr content in the LayZr1-yOx film is above 30% i.e. if the pulse ratio between the lanthanum precursor and the zirconium precursor is larger than six. We study this clustering phenomena using High resol...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Phase Equilibria and Diffusion
سال: 2011
ISSN: 1547-7037,1863-7345
DOI: 10.1007/s11669-011-9862-5