Dynamic Shear Behaviour of Unweldable Aluminum-Scandium (Al-Sc) Alloy
This study uses a torsional split-Hopkinson bar to investigate the shear response and fracture characteristics of unweldable Al-Sc alloy during mechanical testing at shear strain rates of 800 s , 1500 s , 2200 s 1 and 2800 s 1 and temperatures of 150 C, 25 C and 300 C. The experimental results show that both the shear strain rate and the temperature have a significant effect on the shear proper...
متن کاملLaser-induced damage in composites of scandium, hafnium, aluminum oxides with silicon oxide in the infrared.
The laser-induced damage of mixtures of Sc2O3, HfO2, Al2O3 with SiO2 has been characterized in the infrared for both nanosecond and subpicosecond pulses. Laser-induced damage thresholds (LIDTs) are reported and discussed versus band gap for different compositions. The distributions versus fluence of nanosecond damage precursor densities are extracted fitting damage probability curves. Two model...
متن کاملThe Properties and Application of Scandium-Reinforced Aluminum
Scandium-reinforced aluminum alloys represent a new generation of high-performance alloys that display numerous advantages over high-strength aluminum alloys. Scandium-reinforced alloys are much stronger than other high-strength alloys, exhibit significant grain refinement, strengthen welds, and eliminate hot cracking in welds. These alloys also exhibit a good resistance to corrosion as shown b...
متن کاملEffects of Li additions on precipitation-strengthened Al–Sc and Al–Sc–Yb alloys
Two Al–Sc-based alloys (Al–0.12Sc and Al–0.042Sc–0.009Yb, at.%) and their counterparts with Li additions (Al–2.9Li–0.11Sc and Al–5.53Li–0.048Sc–0.009Yb, at.%) are aged at 325 C. For both base alloys, the addition of Li results in greater peak hardness from incorporation of Li in the L12-structured a-Al3(Sc,Li) and a-Al3(Sc,Li,Yb) precipitates, and a concomitant increase in number density and vo...
متن کاملFRACTIONAL RECRYSTALLIZATION KINETICS IN DIRECTLY COLD ROLLED Al-Mg, Al-Mg-Sc AND Al-Mg-Sc-Zr ALLOY
The evaluation of texture as a function of recrystallization has been characterized for directly cold rolled Al-6Mg, Al-6Mg-0.4Sc and Al-6Mg-0.4Sc-0.2Zr alloys. Samples were annealed isothermally at 400 °C for 1 to 240 minutes to allow recrystallization. Recrystallization kinetics of the alloys is analyzed from the micro-hardness variation. Isothermally annealed samples of aluminum alloys were ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Phase Equilibria and Diffusion
سال: 2011
ISSN: 1547-7037,1863-7345
DOI: 10.1007/s11669-011-9923-9