Aging Effect of Mg-Sc Alloy with α+β Two-Phase Microstructure
Mg-20.5 at% Sc alloy with hcp (α)+bcc (β) two-phase was investigated to understand the effects of aging treatment at 473 K on microstructure, hardness and tensile properties. A Mg-Sc alloy ingot was prepared by induction melting in an Ar atmosphere, and then hot rolled at 873 K followed by cold rolling into a sheet. The rolled specimens were annealed at 873 K to obtain an α+β two-phase microstr...
متن کاملMicrostructure and Aging Behavior of Nonflammable AZ91D Mg Alloy
Phase equilibria of AZ91D Mg alloys for nonflammable use, containing Ca and Y, were carried out by using FactSage® and FTLite database, which revealed that solid solution treatment could be performed at temperatures from 400 to 450C. Solid solution treatment of AZ91D Mg alloy without Ca and Y was successfully conducted at 420C and supersaturated microstructure with all beta phase resolved into ...
متن کاملFRACTIONAL RECRYSTALLIZATION KINETICS IN DIRECTLY COLD ROLLED Al-Mg, Al-Mg-Sc AND Al-Mg-Sc-Zr ALLOY
The evaluation of texture as a function of recrystallization has been characterized for directly cold rolled Al-6Mg, Al-6Mg-0.4Sc and Al-6Mg-0.4Sc-0.2Zr alloys. Samples were annealed isothermally at 400 °C for 1 to 240 minutes to allow recrystallization. Recrystallization kinetics of the alloys is analyzed from the micro-hardness variation. Isothermally annealed samples of aluminum alloys were ...
متن کاملMicrostructure Modelling of Hot Deformation of Al-1%Mg Alloy
This study presents the application of the finite element method and intelligent systems techniques to the prediction of microstructural mapping for aluminium alloys. Here, the material within each finite element is defined using a hybrid model. The hybrid model is based on neuro-fuzzy and physically based components and it has been combined with the finite element technique. The model simulate...
متن کاملEffect of Mg addition on the creep and yield behavior of an Al–Sc alloy
The relationships between microstructure and strength were studied at room temperature and 300 °C in an Al–2 wt% Mg–0.2 wt% Sc alloy, containing Mg in solid-solution and Al3Sc (L12 structure) as nanosize precipitates. At room temperature, the yield strength is controlled by the superposition of solid-solution and precipitation strengthening. At 300 °C and at large applied stresses, the creep st...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATERIALS TRANSACTIONS
سال: 2016
ISSN: 1345-9678,1347-5320
DOI: 10.2320/matertrans.m2016093