Aging behavior of Al-4.5%Mg, Al-4.5%Mg-0.35%Mn and Al-1.3%Mg-1.1%Mn alloys containing 0.2%Cu.

نویسندگان
چکیده

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Precipitation evolution in Al–0.1Sc, Al–0.1Zr and Al–0.1Sc–0.1Zr (at.%) alloys during isochronal aging

Precipitation strengthening is investigated in binary Al–0.1Sc, Al–0.1Zr and ternary Al–0.1Sc–0.1Zr (at.%) alloys aged isochronally between 200 and 600 C. Precipitation of Al3Sc (L12) commences between 200 and 250 C in Al–0.1Sc, reaching a 670 MPa peak microhardness at 325 C. For Al–0.1Zr, precipitation of Al3Zr (L12) initiates between 350 and 375 C, resulting in a 420 MPa peak microhardness at...

متن کامل

Microstructure of Al-Zn and Zn-Al Alloys*

The change of microstructure of the title alloys with concentration, temperature and applied thermal treatment was studied in situ by XRD. The alloys, having the Zn atomic fraction, x(Zn), from 0.03 to 0.62, were subjected to: (i) rapid quenching from a temperature, Tt, higher than the solid-solution temperature, Tss, in water at RT (samples WQ); (ii) slow cooling from Tt to RT (samples SC). Th...

متن کامل

Precipitation evolution in Al–Zr and Al–Zr–Ti alloys during aging at 450–600 C

The transformation of Al3Zr (L12) and Al3(Zr1 xTix) (L12) precipitates to their respective equilibrium D023 structures is investigated in conventionally solidified Al–0.1Zr and Al–0.1Zr–0.1Ti (at.%) alloys aged isothermally at 500 C or aged isochronally in the range 300– 600 C. Titanium additions delay neither coarsening of the metastable L12 precipitates nor their transformation to the D023 st...

متن کامل

Influence of Natural Aging Time on Two-Step Aging Behavior of Al-Mg-Si(-Cu) Alloys

Nanoclusters formed during natural aging cause the negative effect of the two-step aging in the age-hardenable Al-Mg-Si alloys. The relationship between the clustering behavior during natural aging and the two-step aging behavior was studied using the hardness, differential scanning calorimetry (DSC), electrical resistivity measurements, transmission electron microscopy (TEM) observation in the...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: Journal of Japan Institute of Light Metals

سال: 1992

ISSN: 0451-5994

DOI: 10.2464/jilm.42.78