Acoustic Emission-Based Methodology to Evaluate Delamination Crack Growth Under Quasi-static and Fatigue Loading Conditions
نویسندگان
چکیده
منابع مشابه
Fatigue crack growth characteristics of Fe and Ni under cyclic loading using a quasi-continuum method
A quasi-continuum (QC) method based on the embedded atom method (EAM) potential was employed to investigate the fatigue crack growth and expansion characteristics of single-crystal Fe and Ni under cyclic loading modes I and II. In particular, the crack growth and expansion characteristics of Fe and Ni under cyclic loading were evaluated in terms of atomic stress fields and force–distance curves...
متن کاملFatigue of polycrystalline silicon for microelectromechanical system applications: crack growth and stability under resonant loading conditions
Although bulk silicon is not known to exhibit susceptibility to cyclic fatigue, micron-scale structures made from silicon films are known to be vulnerable to degradation by fatigue in ambient air environments, a phenomenon that has been recently modeled in terms of a mechanism of sequential oxidation and stress-corrosion cracking of the native oxide layer. To date, most stress-life (S=N ) fatig...
متن کاملIn-situ ultrasonic monitoring of crack growth under static and dynamic loading conditions [5767-1]
Successful in-situ monitoring of crack initiation and growth is a necessary prerequisite for applying ultrasonic methods to structural health monitoring. For conventional ultrasonic testing methods, a focused beam may be used to directly image the crack tip; however, this method is difficult to apply during fatigue testing because of access limitations and couplant contamination issues. However...
متن کاملAnalyses of Fatigue and Fatigue-crack Growth under Constant- and Variable-amplitude Loading
Studies on the growth of small cracks have led to the observation that fatigue life of many engineering materials is primarily “crack growth” from micro-structural features, such as inclusion particles, voids, slip-bands or from manufacturing defects. This paper reviews the capabilities of a plasticity-induced crack-closure model to predict fatigue lives of metallic materials using “small-crack...
متن کاملAcoustic emission during fatigue of Ti-6AI-4V: incipient fatigue crack detection limits and generalized data analysis methodology
The fundamentals associated with acoustic emission monitoring of fatigue crack initiation and propagation of Ti-6AI-4V were studied. Acoustic emission can detect and locate incipient fatigue crack extensions of approximately 1 0 gm. The technique therefore can serve as a sensitive warning to material failure. There are three distinct stages during which acoustic emission is generated. These sta...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Nondestructive Evaluation
سال: 2017
ISSN: 0195-9298,1573-4862
DOI: 10.1007/s10921-017-0454-0