Achieving microstructures prone to superplastic deformation in an Al–Zn–Mg–Cu alloy by equal channel angular pressing
نویسندگان
چکیده
منابع مشابه
Achieving microstructures prone to superplastic deformation in an Al - Zn - Mg - Cu alloy by equal channel angular pressing
An Al-Zn-Mg-Cu alloy without Sc or Zr additions was subjected to overaging and processing by equal channel angular pressing, obtaining a grain size of ∼160 nm and a fraction of high-angle boundaries of 56%. The high elongations attained at high strain rate (10-10 s) and low test temperature (250-300 oC) are attributed to the formation of new recrystallized grains, ∼500 nm in size, during heatin...
متن کاملAchieving superplastic properties in a ZK10 magnesium alloy processed by equal-channel angular pressing
Equal-channel angular pressing provides an opportunity for refining the grain structure and introducing superplastic properties in magnesium alloys. This report describes the use of this processing technique with a ZK10 (Mg–1.0 wt.% Zn–0.26 wt.% Zr) alloy. The grain structure was successfully refined from ∼12.9 to ∼5.2 m after 4 passes and superplastic elongations were observed when testing at ...
متن کاملRe-strengthening in AA6063 Alloy During Equal Channel Angular Pressing
Equal channel angular pressing (ECAP) is carried out using two different configurations for the exit channel of the ECAP die, i.e., relieved and choked, with angles of 0.2 °. It is found that using a die with relieved exit channel, the sample was extruded for 6 passes with no surface cracks and an average cell size of 727 nm and a fraction of high angle grain boundaries of 54 % were achieved. M...
متن کاملCharacteristics of Cavitation in a Superplastic Magnesium Az31 Alloy Processed by Equal- Channel Angular Pressing
Experiments were conducted on a magnesium AZ31 alloy to evaluate the role of cavitation in high temperature superplasticity. Samples were processed by equal-channel angular pressing (ECAP) and then pulled to failure in tension at a temperature of 623K. Similar tests were also conducted on the as-received alloy. The results show the development of significant internal cavitation in this alloy wh...
متن کاملPlastic deformation of 7075 Aluminum Alloy using Integrated Extrusion-Equal Channel Angular Pressing
Grain refinement improves the mechanical properties and formability of metals and alloys. So far, several different grain refinement methods have been proposed and studied. Severe plastic deformation is one of the most promising and efficient methods. Therefore, in the present study the possibility of imposing a two-step severe plastic deformation (Extrusion and Equal channel angular pressing) ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Alloys and Compounds
سال: 2013
ISSN: 0925-8388
DOI: 10.1016/j.jallcom.2012.08.084