Ablation properties of ZrC-SiC-HfB2 ceramic with different amount of carbon fiber under an oxyacetylene flame
نویسندگان
چکیده
منابع مشابه
Fabrication and inspection of C/Cf-ZrB2-ZrC-SiC and C/Cf-ZrB2-SiC composite parts resistant to ablation by pressureless sintering method
In this research, the aim is to achieve strong and ablation-resistant composite parts C / Cf-ZrB2-ZrC-SiC and C / Cf-ZrB2-SiC by non-pressure sintering method. C / Cf-ZrB2-SiC samples were prepared using synthesized ZrB2 and SiC powders between layers of resin-impregnated carbon fabric. After pressing with pressure 5 times at 1600 وC and heat treatment for 2 hours in a controlled atmosphere fur...
متن کاملinvestigation of gassing behavior, electric and dielectric properties of different insulating fluids.
ترانسفورماتورهای قدرت از اجزای اصلی شبکه تامین انرژی الکتریکی می باشند که عملکرد قابل اطمینان ترانسفورماتورها یکی از فاکتورهای مهم و تعیین کننده در تامین انرژی الکتریکی محسوب می شود. در نتیجه بررسی و مانیتور عملکرد ترانسفورماتورها در شبکه و همچنین عیب یابی این ترانسفورماتورها غیرقابل اجتناب و ضروری می باشد. به طور کلی عایق های مایع در صنعت فشار قوی کاربردهای متفاوتی دارند که مهمترین وظیفه آنها...
15 صفحه اولinvestigation of the electronic properties of carbon and iii-v nanotubes
boron nitride semiconducting zigzag swcnt, $b_{cb}$$n_{cn}$$c_{1-cb-cn}$, as a potential candidate for making nanoelectronic devices was examined. in contrast to the previous dft calculations, wherein just one boron and nitrogen doping configuration have been considered, here for the average over all possible configurations, density of states (dos) was calculated in terms of boron and nitrogen ...
15 صفحه اولC/C-ZrB2-ZrC-SiC Composite Derived from Polymeric Precursor Infiltration and Pyrolysis Part 2: Mechanical and Ablation Properties
Mechanical and ablation properties of the 2D C/C-ZrB2-ZrC-SiC composites with a fiber volume fraction of 17.6%, fabricated by infiltration and co-pyrolysis of blended polymeric precursors, were studied in this Part II. Flexural strength and fracture toughness of the composites were found to be influenced strongly by the thickness of the deposited pyrolytic carbon interphase, a composite with th...
متن کاملcontrol of the optical properties of nanoparticles by laser fields
در این پایان نامه، درهمتنیدگی بین یک سیستم نقطه کوانتومی دوگانه(مولکول نقطه کوانتومی) و میدان مورد مطالعه قرار گرفته است. از آنتروپی ون نیومن به عنوان ابزاری برای بررسی درهمتنیدگی بین اتم و میدان استفاده شده و تاثیر پارامترهای مختلف، نظیر تونل زنی(که توسط تغییر ولتاژ ایجاد می شود)، شدت میدان و نسبت دو گسیل خودبخودی بر رفتار درجه درهمتنیدگی سیستم بررسی شده اشت.با تغییر هر یک از این پارامترها، در...
15 صفحه اولذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials Research Express
سال: 2020
ISSN: 2053-1591
DOI: 10.1088/2053-1591/ab70db